LUVOCOM® 65-7311

Категория	PP, Polypropylene Copolymer , PP Copolymer
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	KnMKfg_LUVOCOM-65-7311.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®65-7311 is a polypropylene copolymer (PP Copoly) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 65-7311 are:

Conductivity

Electrostatic protection

anti-warping

Good stiffness

Главная Информация
Наполнитель/армирование	Армированный материал из углеродного волокна
Характеристики	Проводящий Низкий уровень защиты Жесткий, хороший Защита от электростатического разряда Хорошая прочность
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	0.980	g/cm³	ISO 1183
Формовочная усадка	0.30 - 0.70	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	6000	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.0	%	ISO 527-2
Флекторный модуль	5000	MPa	ISO 178
Флекторный стресс	80.0	MPa	ISO 178
Коэффициент трения
Dynamic	0.23
Static	0.15
Flexural Strain at Flexural Strength	4.5	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	130	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0E+4	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	100	°C	UL 746B
Викат Температура размягчения	80.0	°C	ISO 306/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+7	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки	70.0 - 95.0	°C
Время сушки	2.0 - 4.0	hr
Рекомендуемая максимальная влажность	0.20	%
Задняя температура	220 - 250	°C
Средняя температура	220 - 250	°C
Передняя температура	230 - 250	°C
Температура сопла	220 - 250	°C
Температура обработки (расплава)	230 - 260	°C
Температура формы	40.0 - 80.0	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
SABIC® PPcompound 7510	PP, Unspecified	Saudi Basic Industries Corporation (SABIC)
Thermylene® P-30TC-1156	PP, Unspecified	Asahi Kasei Plastics North America Inc.
AIE PP 8010F	PP, Unspecified	Asia International Enterprise (Hong Kong) Limited
MAJORIS DG407X - 8784	PP, Unspecified	AD majoris
POLYFLAM® RIPP 510 D	PP Copolymer	A. Schulman Europe
Hifax CA 1110 G2	PP Impact Copolymer	LyondellBasell Industries