Clearflex® H&T CHH 196
Описание материалов:
Clearflex H&T CHH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.
Stretch films manufactured with Clearflex H&T CHH 196 have outstanding fracture mechanical properties, mainly Elmendorf tear strength along machine direction (MD) and puncture resistance. Moreover, the holding force is the key property of these films when used in automatic wrapping machines.
Main Applications
Clearflex H&T CHH 196 is recommended for production of super-power stretch films. Its properties, especially in terms of holding force and puncture resistance, make Clearflex H&T CHH 196 the ideal choice for packaging goods of irregular shape and for applications requiring a superior mechanical strength.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Гексен-комномер
- Сопротивление перфорации
- Устойчивость к окислению
- Хорошая прочность на разрыв
- Соответствие пищевого контакта
|
| Используется | - Упаковка
- Пленка
- Растягивающаяся обмотка
- Литая пленка
|
| Рейтинг агентства | - Европейский пищевой контакт, не Номинальный
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.916 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (Dynamic, Cast Film) | > 0.50 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 23 | µm | |
| Толщина пленки-рекомендовано/доступно | 8 to 50 µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% sectioning, MD
: 23 µm, cast film | 145 | MPa | ISO 527-3 |
| 1% sectioning, TD
: 23 µm, cast film | 140 | MPa | ISO 527-3 |
| Tensile Stress | | | ISO 527-3 |
| MD
: yield, 23 µm, cast film | 8.00 | MPa | ISO 527-3 |
| TD
: yield, 23 µm, cast film | 9.00 | MPa | ISO 527-3 |
| MD
: fracture, 23 µm, casting film | 40.0 | MPa | ISO 527-3 |
| TD
: fracture, 23 µm, casting film | 32.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: fracture, 23 µm, casting film | 600 | % | ISO 527-3 |
| TD
: fracture, 23 µm, casting film | 800 | % | ISO 527-3 |
| Ударное падение Dart (23 µm, Cast Film) | 330 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 23.0 µm | 130.0 | kN/m | ISO 6383-2 |
| TD
: 23.0 µm | 240.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 95.0 | °C | ISO 306/A |
| Температура плавления | 123 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 23.0 µm, Cast Film) | 92 | | ASTM D2457 |
| Haze (23.0 µm, Cast Film) | 2.5 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 220 - 270 | °C | |