Chemlon® E-6 GF15

Категория PA6, Polyamide 6 , Nylon 6
Производитель Teknor Apex Company (Chem Polymer)
Торговая марка Chemlon®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF KMrlby_Chemlon-E-6-GF15.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Chemlon® E-6 GF15 is an economy range 15% glass fibre reinforced Nylon 6 compound.
It is available in natural or black versions.
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал, 15% наполнитель по весу
Внешний вид
  • Черный
  • Натуральный цвет
Метод обработки
  • Литье под давлением
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.24g/cm³ISO 1183
Формовочная усадка 10.60 - 1.0%Internal method
Поглощение воды (Equilibrium, 23°C, 50% RH)2.3%ISO 62
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 5500MPaISO 527-2
Tensile Stress (Break)105MPaISO 527-2
Растяжимое напряжение (Break)3.0%ISO 527-2
Флекторный модуль 5000MPaISO 178
Флекторный стресс 2150MPaISO 178
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Зубчатый изод Impact 5.0kJ/m²ISO 180
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature
    0.45 MPa, not annealed > 190°CISO 75-2/B
    1.8 MPa, not annealed 175°CISO 75-2/A
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки 80.0°C
Время сушки 2.0hr
Задняя температура 230 - 260°C
Средняя температура 230 - 260°C
Передняя температура 230 - 260°C
Температура обработки (расплава) < 300°C
Температура формы 80.0 - 90.0°C
Скорость впрыска Fast
Screw Speed 50 - 200rpm
Инструкции по впрыску
Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.
Примечание
1 .Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .At Break
Тип материала Категория Производитель
Generic Nylon 6 - Glass Fabric Nylon 6 Generic
VITAMIDE® BI10 Nylon 6 A. Schulman Europe
VAMPAMID 6 3028 V2 MF Nylon 6 Vamp Tech
ESTOPLAST XU 230HSBB11 Nylon 6 Ester Industries Ltd.
Durethan® BKV 30 G W1 901317 Nylon 6 LANXESS Asia/Pacific
Durethan® BM 430 H2.0 901510 Nylon 6 LANXESS GmbH
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат

Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.

Служба поддержки клиентов Вичат
Свяжитесь с нами