LUVOCOM® 1-RG 4

Категория	PA66, Polyamide 66 , Nylon 66
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	KAZofv_LUVOCOM-1-RG-4.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1-RG 4 is a polyamide 66 (nylon 66) material that contains a carbon fiber reinforced material. This product is available in Europe,.

LUVOCOM®The main features of 1-RG 4 are:

Conductivity

High stiffness

high strength

Electrostatic protection

Good dimensional stability

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Армированный материал из углеродного волокна
Добавка	Ptfe лубрикант Стабилизатор тепла
Характеристики	Хорошая стабильность размеров Проводящий Низкий коэффициент трения Жесткий, высокий Высокая прочность Защита от электростатического разряда Хорошая стойкость к истиранию Термическая стабильность Смазка
Используется	Шестерня Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование Камера
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.33	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.30	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 1.0	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	15000	MPa	ISO 527-2
Tensile Stress (Break)	205	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.4	%	ISO 527-2
Флекторный модуль	13000	MPa	ISO 178
Флекторный стресс	310	MPa	ISO 178
Коэффициент трения
Dynamic	0.19
Static	0.12
Flexural Strain at Flexural Strength	3.3	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	160	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	120	°C	UL 746B

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Время сушки
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.10	%
Задняя температура	290 - 310	°C
Средняя температура	290 - 310	°C
Передняя температура	290 - 310	°C
Температура сопла	280 - 300	°C
Температура обработки (расплава)	290	°C
Температура формы	90.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Bergamid鈩?A70 G25 H U-SO	Nylon 66	PolyOne Corporation
DESLON™ 66 DSC201G3	Nylon 66	DESCO Co., Ltd.
GERMAMID 6.6 GF 30 H	Nylon 66	Kunststoff-Kontor-Hamburg GmbH
Hyundai EP PA66 LD140	Nylon 66	HYUNDAI EP Co., Ltd.
Ultramid® A3WG10	Nylon 66	BASF Corporation
Chemlon® AS408	Nylon 66	Teknor Apex Company (Chem Polymer)

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

