DOW™ Electrical & Telecommunications DFDA-1675 NT

Категория	PO, Non-Halogen, Flame Retardant, Thermoplastic Jacket Compound , Polyolefin, Unspecified
Производитель	The Dow Chemical Company
Торговая марка	DOW™ Electrical & Telecommunications
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	IwAwhd_DOW-Electrical-Telecommunications-DFDA-1675-NT.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Halogen-free flame retardant material, used for communication cables and sheathing materials

DFDA-1675 NT is a halogen-free flame retardant polyolefin thermoplastic material, used as a material for communication cables and sheathing. DFDA-1675 NT has excellent electrical properties, flame retardant grade, processability and flexibility. After the official launch, DFDA-1675 NT will be called UNIGARD™RE DFDA-1675 NT.

Features
DFDA-1675 NT has the following characteristics:

high flame retardant performance

Excellent electrical properties and moisture resistance

Environmental protection (lead-free, halogen-free, sulfur-free/antimony-free)

low smoke, low corrosion and low toxicity

Has a good balance between toughness and flexibility

The extrusion process is easy, no special screw is required

compliance with ROHS regulations

Recommendations and specifications for use
DFDA-1675 NT is a transverse substrate material for Plenum Category 6 communication cables that require UL NFPA 262 combustion test grades. This combustion grade depends on the cable structure and requires separate testing and certification. Each manufacturer using DFDA-1675 NT must consult a standard testing organization to determine which tests and evaluations (if any) are required to obtain application certification.

Главная Информация
Используется	Огнезащитный кожух Кабельный сепаратор LAN LSZH Куртка Применение проводов и кабелей
Рейтинг агентства	UL NFPA 262
Формы	Частицы

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	1.54	g/cm³	ASTM D792

Твердость	Номинальное значение	Метод испытания
Твердость дюрометра ¹		ASTM D2240
Shaw A	96	ASTM D2240
Shaw D	41	ASTM D2240

Механические	Номинальное значение	Единица измерения	Метод испытания
Прочность на растяжение ²	> 8.96	MPa	ASTM D638
Удлинение при растяжении ³(Break)	> 120	%	ASTM D638
Флекторный модуль- 1% Secant ⁴	265	MPa	ASTM D790

Электрический	Номинальное значение	Метод испытания
Диэлектрическая постоянная		ASTM D150
1 MHz ⁵	3.24	ASTM D150
1 MHz	3.25	ASTM D150
Коэффициент рассеивания ⁶(1 MHz)	1.2E-3	ASTM D150

Воспламеняемость	Номинальное значение	Единица измерения	Метод испытания
Индекс кислорода ⁷	38	%	ASTM D2863
Тест на сжигание Пленума- Поперечный сепаратор в кошке. 6 конструкция	PASS		UL NFPA 262

Дополнительная информация
Colorability DFDA-1675 NT EXP1 is a colorable compound. The color masterbatch materials recommended for use with polyethylene or ethylene copolymer wire and cable products are suitable for use in DFDA-1675 NT EXP1. Where optimal electrical performance is required, use a polyethylene homopolymer based color masterbatch to avoid deterioration of dielectric properties. Generally speaking, color masterbatch added at the level from 0.5 to 1.0% by weight gives adequate color and disperses well in the extrusion process. For black jacket applications, UV resistance can be also achieved by adding a carbon black masterbatch. However, the level may be higher, and depends on the type of carbon black masterbatch and the test requirement for the application.

Дополнительная информация

Colorability DFDA-1675 NT EXP1 is a colorable compound. The color masterbatch materials recommended for use with polyethylene or ethylene copolymer wire and cable products are suitable for use in DFDA-1675 NT EXP1. Where optimal electrical performance is required, use a polyethylene homopolymer based color masterbatch to avoid deterioration of dielectric properties. Generally speaking, color masterbatch added at the level from 0.5 to 1.0% by weight gives adequate color and disperses well in the extrusion process. For black jacket applications, UV resistance can be also achieved by adding a carbon black masterbatch. However, the level may be higher, and depends on the type of carbon black masterbatch and the test requirement for the application.

Экструзия	Номинальное значение	Единица измерения
Зона цилиндра 1 темп.	127	°C
Зона цилиндра 2 температура.	191	°C
Зона цилиндра 3 темп.	191	°C
Зона цилиндра 4 темп.	191	°C
Зона цилиндра 5 темп.	204	°C
Температура матрицы	204	°C

Инструкции по экструзии
螺杆类型：单跨测量螺杆螺杆 L/D 20:1 至 24:1压缩比 2.5:1 至 3.5:1筛网组 60/20、40/20 或 20 网孔模具压力/或管子打开下拉比 1.0 比 1.5螺杆冷却：无

Примечание
1 .	Based on plaques
2 .	Based on tapes produced with a 20 mil die and draw down to 17 mils
3 .	Based on tapes produced with a 20 mil die and draw down to 17 mils
4 .	Based on tapes produced with a 20 mil die and draw down to 17 mils
5 .	Aged 4 weeks, 90°F (32°C) and 90% Relative Humidity
6 .	Aged 4 weeks, 90°F (32°C) and 90% Relative Humidity
7 .	Based on plaques

Тип материала	Категория	Производитель
Generic Polyolefin, Unspecified - Calcium Carbonate	Polyolefin, Unspecified	Generic
Softell TBP 237D NAT	Polyolefin, Unspecified	LyondellBasell Industries
T & T Marketing PR-2003 Black	Polyolefin, Unspecified	T & T Marketing, Inc.
INTEGRAL™ 625	Polyolefin, Unspecified	The Dow Chemical Company
CALSIN SE105	Polyolefin, Unspecified	Pooya Polymer Tehran
CALP MRP312	Polyolefin, Unspecified	Lion Idemitsu Composites Co., Ltd.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

