Описание материалов:
TECASON® P MT is a polyphenylsulfone suited primarily to applications in the medical industry. It is in the same performance category as products like Polysulfone and ULTEM® polyetherimide. TECASON® P MT has improved performance in terms of temperature, impact strength and chemical resistance. TECASON® P MT also has exceptional resistance to repeated steam autoclaving without loss of dimensional stability or physical properties. TECASON® PMT is available in several colored and transparent grades, as well as with our x-ray opaque XRO additive which allows for clear component visibility on fluorscopy and x-ray.
TECASON® P MT series products are targeted at a number of applications in the medical industry.TECASON® P MT is often used in applications for surgical tools and instruments because of its resistance to autoclave sterilization damage. A second market for TECASON®, it is also a popular material choice for trials used in joint replacement surgeries.
| Главная Информация | |
|---|
| Характеристики | - Высокий уровень ЭСКП (устойчивость к растрескиванию)
- Высокая прочность на растяжение
- Высокая прочность
- Термостойкость высокого давления
- Теплостойкость, высокая
|
| Используется | - Хирургические инструменты
- Медицинские принадлежности/принадлежности для ухода
|
| Внешний вид | - Непрозрачный
- Доступные цвета
- Прозрачный/прозрачный
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.29 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 23°C, 24 hr | 0.37 | % | ASTM D570 |
| Saturated, 23°C | 1.1 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 123 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2340 | MPa | ASTM D638 |
| Прочность на растяжение (Yield, 23°C) | 69.6 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 23°C) | 60 | % | ASTM D638 |
| Флекторный модуль (23°C) | 2410 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 91.0 | MPa | ASTM D790 |
| Прочность на сжатие | 98.9 | MPa | ASTM D695 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Незубчатый изод Impact | 690 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 214 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 207 | °C | ASTM D648 |
| Викат Температура размягчения | 218 | °C | |
| CLTE-
Поток (-40 to 38°C) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Удельный нагрев | 1130 | J/kg/°C | ASTM C351 |
| Максимальная температура обслуживания-
Прерывистый | 182 | °C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | 1.0E+15 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность | 14 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная 1(23°C, 60 Hz) | 3.44 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from injection molded samples. |