OnForce™ LFT AM-30LCF/001 Grey
Описание материалов:
Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Длинное углеродное волокно, 30% наполнитель по весу
|
| Характеристики | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.30 | g/cm³ | ISO 1183 |
| Формовочная усадка 1 | 0.20 | % | ISO 294-4 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 25000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 280 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break) | 1.5 | % | ISO 527-2 |
| Флекторный модуль | 21000 | MPa | ISO 178 |
| Флекторный стресс | 400 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 48 | kJ/m² | ISO 179 |
| Ударное падение Dart | 6.33 | J | ASTM D5420 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 120 | °C | |
| Время сушки | 4.0 | hr | |
| Температура обработки (расплава) | 290 - 320 | °C | |
| Температура формы | 140 | °C | |
| Скорость впрыска | Slow-Moderate | | |
| Back Pressure | 1.00 | MPa | |
| Инструкции по впрыску |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed. |
| Примечание |
|---|
| 1 . | Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions. |