Bayflex WR-80 is a solid elastomer which has a flexural modulus of 10,000 psi (69 MPa) at room temperature. It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics, and outstanding physical properties. The Bayflex WR-80 system was developed to add a weather-resistant grade to our range of window encapsulation systems.
In some cases, the weatherability of this system eliminates the need for post-painting or in-mold coatings. This product is available only in black. Bayflex WR-80 is a formulated RIM system supplied as two reactive liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and component B is a polyether polyol. As with any product, use of the Bayflex WR-80 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Хорошая устойчивость к погоде
- Хорошая производительность при потере
|
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.03 | g/cm³ | ASTM D1622 |
| Формовочная усадка-
Поток | 1.5 | % | Internal method |
| Поглощение воды (24 hr) | 3.3 | % | Internal method |
| Скорость поглощения воды-
240 hr | 6.4 | % | Internal method |
| Старение | Номинальное значение | | Метод испытания |
|---|
| Выдержка атмосферометра-
Дельта е 1 | 14.0 | | SAE J2527 |
| Тепловой | Номинальное значение | | Метод испытания |
|---|
| Низкая температура ломкости (-50°C) | No Cracking | | ASTM D746 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Погружение в воду, увеличение длины | 1.4 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 91 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Флекторный модуль | | | ASTM D790 |
| -30°C | 215 | MPa | ASTM D790 |
| 23°C | 68.9 | MPa | ASTM D790 |
| 65°C | 45.5 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 17.2 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 300 | % | ASTM D412 |
| Tear Strength 2 | 79.2 | kN/m | ASTM D624 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта 3 | | | |
| Component a | Mixing ratio by weight: 37 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Время демолд | 0.50 | min | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Part A
Type: Isocyanate
Specific Gravity @ 25°C: 1.21
Viscosity @25°C: 700 mPa-s
Flash Point PMCC: 213 °C
Part B
Type: Polyol
Specific Gravity @ 25°C: 1.02
Viscosity @25°C: 1400 mPa-s
Flash Point PMCC: 184 °C
Molding Parameters
Material Temperature: 32 to 42 °C
Mold Temperature: 60 to 70 °C |
| Примечание |
|---|
| 1 . | ASTM G155, cycle 7 @ 2500 kJ/m², Atlas CXW Open Flame |
| 2 . | C mould |
| 3 . | 105 Index |