- Braskem PE SGM9450F
Braskem PE SGM9450F
| Категория | HDPE, High Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
IRkKyQ_BraskemPESGM9450F.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Description:
SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process.
The minimum biobased content of this grade is 96%, determined according to ASTM D6866.
Application:
Bags in general (like T-shirt bags, Handle Bags, Star Bags, others);
Geomembranes.
SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process.
The minimum biobased content of this grade is 96%, determined according to ASTM D6866.
Application:
Bags in general (like T-shirt bags, Handle Bags, Star Bags, others);
Geomembranes.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.952 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 9.3 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.33 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 13 µm | 40.0 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 30.0 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 85.0 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 45.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 13 µm | 590 | % | ASTM D882 |
| TD : Broken, 13 µm | 740 | % | ASTM D882 |
| Ударное падение Dart 1 | 250 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 58 | g | ASTM D1922 |
| TD : 13 µm | 51 | g | ASTM D1922 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Puncture Resistance (12.5 µm) | 80.0 | J/m | Internal method |
| Запечатывание начальной температуры | 125 | °C | Internal method |
| Двуслойное содержание | > 96 | % | ASTM D6866 |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| RELENE® HD53MA020 | HDPE | Reliance Industries Limited |
| TAISOX 7501 | HDPE | Formosa Plastics Corporation |
| BorSafe™ HE3498-LS-H | HDPE | Borealis AG |
| EL-Lene™ H5615F | HDPE | SCG Chemicals Co., Ltd. |
| Halene H M5025L | HDPE | Haldia Petrochemicals Ltd. |
| Hanwha Total PE R902U | HDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved