Описание материалов:

Bayflex 963 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system.

The Bayflex 963 system is used in the manufacture of microcellular polyurethane innersoles. The innersoles prepared from these compounds combine light weight, comfort, and durability.

Processibility and dynamic flexural properties are excellent and have made the Bayflex 963 system a prime innersole material. As with any product, use of the Bayflex 963 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

The properties of the Bayflex 963 system, listed below, are representative of typical performance characteristics of molded panels. Actual results may vary, depending on part design and processing conditions.

Главная Информация
Характеристики	Обрабатываемость, хорошая Хорошая гибкость
Используется	Обувь

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	0.304	g/cm³	Internal method

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра	60		ASTM D2240

Эластомеры	Номинальное значение	Единица измерения	Метод испытания
Прочность на растяжение (Break)	2.07	MPa	ASTM D412
Удлинение при растяжении (Break)	500	%	ASTM D412
Tear Strength ¹	1.40	kN/m	Internal method
Отклонение сжатия при 25%	0.0517	MPa	ASTM D575
Отклонение сжатия при 50%	0.138	MPa	ASTM D575
Комплект сжатия (25°C, 22 hr)	4.0	%	ASTM D395

Термокомплект	Номинальное значение
Компоненты термокомплекта
Component a	Mixing ratio by weight: 69
Component B	Mixing ratio by weight: 100

Дополнительная информация
Part A Type: Isocyanate Appearance: Light yellow viscous liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPas Flash Point PMCC: 207°C Bulk Density @ 20°C:10.01 lb/gal NCO: 18.7 - 19.1 wt% Part B Type: Polyol Appearance: Milky white liquid Specific Gravity @ 25°C: 1.06 Viscosity @25°C: 1100 mPas Flash Point PMCC: 126°C Bulk Density @ 25°C: 8.85 lb/gal Water: 0.83 wt% Hydroxyl Number: 125 Material Temperature: 25 to 30°CMold Temperature: 43 to 49°CDemold Time: 3.5 minLinear Shrinkage@ 0.5 g/cm: <1.0%Hand Mix Reactivity @ 25°C Cream Time: 10 to 15 sec Tack Free: 45 to 55 sec Pull Time: 55 to 65 sec Free-Rise Density: 8 to 11 lb/ft³

Дополнительная информация

Part A Type: Isocyanate Appearance: Light yellow viscous liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPa*s Flash Point PMCC: 207°C Bulk Density @ 20°C:10.01 lb/gal NCO: 18.7 - 19.1 wt% Part B Type: Polyol Appearance: Milky white liquid Specific Gravity @ 25°C: 1.06 Viscosity @25°C: 1100 mPa*s Flash Point PMCC: 126°C Bulk Density @ 25°C: 8.85 lb/gal Water: 0.83 wt% Hydroxyl Number: 125 Material Temperature: 25 to 30°CMold Temperature: 43 to 49°CDemold Time: 3.5 minLinear Shrinkage@ 0.5 g/cm: <1.0%Hand Mix Reactivity @ 25°C Cream Time: 10 to 15 sec Tack Free: 45 to 55 sec Pull Time: 55 to 65 sec Free-Rise Density: 8 to 11 lb/ft³

Примечание
1 .	Block

Тип материала	Категория	Производитель
Tool-A-Thane UT-505	PUR, Unspecified	Urethane Tooling & Engineering Corp
Vibrathane® B844	PUR-Ether/TDI	Chemtura
Andur 8-APF-LM/Curene® 3005	PUR-Ester/TDI	Anderson Development Company
Huafon JF-W-H3050	PUR, Unspecified	Huafon Group Co., Ltd.
Andur 2-920 AP/Curene® 442	PUR-Est/eth,TDI	Anderson Development Company
RTP 2303 A TFE 15	PUR, Unspecified	RTP Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

