Описание материалов:
Andur M-33 is a low melting MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in low temperature applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 81 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.241 | MPa | ASTM D695 |
| 5% strain | 0.655 | MPa | ASTM D695 |
| 10% strain | 1.38 | MPa | ASTM D695 |
| 15% strain | 2.14 | MPa | ASTM D695 |
| 20% strain | 2.90 | MPa | ASTM D695 |
| 25% strain | 3.72 | MPa | ASTM D695 |
| 50% strain | 10.1 | MPa | ASTM D695 |
| Устойчивость к истиранию | 10.5 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 5.65 | MPa | ASTM D412 |
| 300% strain | 9.38 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 46.2 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 480 | % | ASTM D412 |
| Комплект сжатия | 45 | % | ASTM D395 |
| Сопротивляемость Bayshore | 30 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 11 - 13 | min | |
| Время демолд | 75 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 410 pliAverage Split Tear, ASTM D1938: 50 pliStoichiometry Curative Level: 97%NBS Abrasion: 185% Rubber StandardParts of curative per 100 parts Andur M-33, 6.75% NCO: 8.11 parts by weightParts of curative per 100 parts Andur M-33, 6.8% NCO: 8.17 parts by weightParts of curative per 100 parts Andur M-33, 6.85% NCO: 8.23 parts by weightParts of curative per 100 parts Andur M-33, 6.9% NCO: 8.29 parts by weightParts of curative per 100 parts Andur M-33, 6.95% NCO: 8.35 parts by weightParts of curative per 100 parts Andur M-33, 7% NCO: 8.41 parts by weightMix Temperature:
Andur M-33: 176-194°F
Curative DEG: 77-158°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 80.0 - 120 | °C | |