Описание материалов:
Menzolit® SMC 1100 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals.
Menzolit® SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific resin and a higher amount of glass fibers results in high mechanical strength. Durability is improved as well. Even without a specific fire retardant, the fire retardancy level HB according UL 94 is achieved. Typical applictions are structural components within the automotive industry or mechanical engineering. It is suitable for load carrying applications or fast moving and accelerated components.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ минеральное, 45% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Без галогенов
- Высокая термостойкость
- Высокая прочность
- Низкий уровень дыма
|
| Используется | - Автомобильные Приложения
- Инженерные приложения
|
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.80 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.040 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 150 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.6 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 13000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 280 | MPa | ISO 178 |
| Сжимающее напряжение | 120 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | | Internal Method |
| Matrix Crazing Strain | 0.60 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 130 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 162 | °C | DSC |
| CLTE-
Поток | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |