Описание материалов:
Baydur 730 IBS is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a modified polymeric diphenylmethane diisocyanate (PMDI) prepolymer blend, and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives.
The Baydur 730 IBS system was designed for general-purpose applications and is used in the construction, agricultural, consumer products, industrial and specialty automotive markets. The applications typically take advantage of the material's strength, as well as its excellent surface finish, large part capability and good flowability. As with any product, use of the Baydur 730 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хороший поток
- Хорошая прочность
- Хорошая поверхность
|
| Используется | - Применение в сельском хозяйстве
- Автомобильные Приложения
- Применение конструкции
- Общее назначение
- Промышленное применение
|
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.638 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | | | ASTM D955 |
| 6.35 mm | 0.70 to 0.90 | % | |
| 12.7 mm | 0.70 to 0.90 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shore D, 6.35 mm | 65 | | |
| Shore D, 12.7 mm | 65 | | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| Break, 6.35 mm | 18.6 | MPa | |
| Break, 12.7 mm | 17.2 | MPa | |
| Удлинение при растяжении | | | ASTM D638 |
| Break, 6.35 mm | 10 | % | |
| Break, 12.7 mm | 12 | % | |
| Флекторный модуль | | | ASTM D790 |
| 6.35 mm | 965 | MPa | |
| 12.7 mm | 896 | MPa | |
| Flexural Strength | | | ASTM D790 |
| 6.35 mm | 34.5 | MPa | |
| 12.7 mm | 37.9 | MPa | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength | | | Internal Method |
| -- 1 | 21 | kJ/m² | |
| -- 2 | 27 | kJ/m² | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed, 6.35 mm | 94.0 | °C | |
| 0.45 MPa, Unannealed, 12.7 mm | 90.0 | °C | |
| Примечание |
|---|
| 1 . | 0.5 |
| 2 . | 0.25 in |