MonoSol® AF L330
| Категория | PVOH, Polyvinyl Alcohol |
| Производитель | MonoSol, LLC |
| Торговая марка | MonoSol® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
GN39Ka_MonoSol-AF-L330.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
MonoSol AF L300 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology.
MonoSol AF L330 is a typical grade of PVOH cold water-soluble packaging film and is the film choice for powders with no special requirements or contraindications. This tough film has good solubility, machinability, toughness and cold crack resistance. It is available in bags and can be converted on most vertical form fill and rotorary forming packaging machines. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil).
MonoSol AF L330 is a typical grade of PVOH cold water-soluble packaging film and is the film choice for powders with no special requirements or contraindications. This tough film has good solubility, machinability, toughness and cold crack resistance. It is available in bags and can be converted on most vertical form fill and rotorary forming packaging machines. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil).
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Содержание влаги (23 °C) 1 | 6.7 | wt% | |
| Растворимость 2 | |||
| Disintegration : 10°C, 60.0 µm | 31.0 | sec | |
| Dissolution : 10°C, 60.0 µm | 95.0 | sec |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Выход (60,0 мкм) | 13.4 | m²/kg | ASTM D4321 |
| Толщина пленки протестирована | 60 | µm | |
| Толщина пленки-рекомендовано/доступно | 20 µm to 80 µm | ||
| Сектантный модуль | ASTM D882, ISO 527-3 | ||
| 10%, MD : 60 µm | 77.9 | MPa | |
| 100%, MD : 60 µm | 26.9 | MPa | |
| 10%, TD : 60 µm | 66.2 | MPa | |
| 100%, TD : 60 µm | 14.5 | MPa | |
| Прочность на растяжение | |||
| MD : Break, 60 µm | 43.4 | MPa | ASTM D882 |
| TD : Break, 60 µm | 32.4 | MPa | ASTM D882 |
| MD : 60 µm | 43.4 | MPa | ISO 527-3 |
| TD : 60 µm | 32.4 | MPa | ISO 527-3 |
| Удлинение при растяжении | ASTM D882, ISO 527-3 | ||
| MD : Break, 60 µm | 220 | % | |
| TD : Break, 60 µm | 380 | % | |
| Elmendorf Tear Strength | |||
| MD : 60 µm | 1300 | g | ASTM D1922 |
| TD : 60 µm | 1300 | g | ASTM D1922 |
| MD : 60 µm | 0.13 | N | ISO 6383-2 |
| TD : 60 µm | 0.13 | N | ISO 6383-2 |
| Примечание | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Тип материала | Категория | Производитель |
|---|---|---|
| Selvol™ ULTALUX FF | PVOH | Sekisui Chemical Company, Ltd. |
| DENKA POVAL K-17U6 | PVOH | Denka Company Limited |
| Selvol™ 513 | PVOH | Sekisui Chemical Company, Ltd. |
| Kuraray Poval® PVA L-9 | PVOH | Kuraray Co., Ltd. |
| Kuraray Poval® PVA 103 | PVOH | Kuraray Co., Ltd. |
| Selvol™ E 203 | PVOH | Sekisui Chemical Company, Ltd. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved