Описание материалов:
Eastar™ copolyester 6763 is a clear, amorphous material. Because of its clarity, toughness and good melt strength at processing temperatures, it is useful in a variety of processing techniques including film and sheet extrusion. Eastar™ Copolyester 6763 may be colored using color concentrates, dry colors or liquid colorants.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
This product has been CRADLE TO CRADLE CERTIFIED Silver.
The CRADLE TO CRADLE CERTIFIED Mark is a registered certification mark used under license through McDonough Braungart Design Chemistry (MBDC). MBDC is a global sustainability consulting and product certification firm. The CRADLE TO CRADLE® framework moves beyond the traditional goal of reducing the negative impacts of commerce ('eco-efficiency'), to a new paradigm of increasing its positive impacts ('eco-effectiveness'). At its core, Cradle to Cradle design perceives the safe and productive processes of nature's 'biological metabolism' as a model for developing a 'technical metabolism' flow of industrial materials. Product components can be designed for continuous recovery and reutilization as biological and technical nutrients within these metabolisms. For more information about MBDC and to obtain printable certificates for Eastman Copolyesters, visit www.mbdc.com. Choose Eastman Chemical Company under Company Name in C2C Certified products to display a list of our products.
| Главная Информация | |
|---|
| Характеристики | - Аморфный
- Стерилизуемый e-луч
- Хорошая цветность
- Хорошая прочность расплава
- Хорошая прочность
- Высокая четкость
- Радиационный стерилизуемый
|
| Используется | - Контейнеры
- Косметическая упаковка
- Электрическое/электронное применение
- Пленка
- Пищевая упаковка
- Мебель
- Этикетка
- Ламинаты
- Медицинские/медицинские приложения
- Упаковка
- Лист
- Термоусадочная пленка
- Спортивные товары
- Тонкостенная упаковка
- Игрушки
- Инструменты для письма
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзионная пленка
- Экструзионный лист
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.27 | g/cm³ | ASTM D792, ASTM D1505 |
| 23°C | 1.27 | g/cm³ | ISO 1183/D |
| Поглощение воды (23°C, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | |
| R-Scale, 23°C | 106 | | ASTM D785 |
| R-Scale, 23°C | 109 | | ISO 2039-2 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 2100 | MPa | ASTM D638, ISO 527-2 |
| Прочность на растяжение | | | ASTM D638, ISO 527-2 |
| Yield, 23°C | 50.0 | MPa | |
| Break, 23°C | 28.0 | MPa | |
| Удлинение при растяжении | | | |
| Break, 23°C | 130 | % | ASTM D638 |
| Break, 23°C | 100 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 2100 | MPa | ASTM D790 |
| 23°C | 2000 | MPa | ISO 178 |
| Флекторный стресс | | | |
| 23°C | 68.0 | MPa | ISO 178 |
| Yield, 23°C | 70.0 | MPa | ASTM D790 |
| Сопротивление разрыву | | | ASTM D2582 |
| MD
: 23°C, 250.0 µm | 93 | N | |
| TD
: 23°C, 250.0 µm | 93 | N | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Проницаемость углекислого газа (23 °C, 250,0 мкм) | 49 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Сопротивление размножению разрыва 1 | | | ASTM D1938 |
| MD
: 23°C, 250.0 µm | 36 | kN/m | |
| TD
: 23°C, 250.0 µm | 36 | kN/m | |
| Толщина пленки протестирована | 250 | µm | |
| Сектантный модуль | | | ASTM D882 |
| MD
: 250 µm | 1900 | MPa | |
| TD
: 250 µm | 1900 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 250 µm | 52.0 | MPa | |
| TD
: Yield, 250 µm | 52.0 | MPa | |
| MD
: Break, 250 µm | 59.0 | MPa | |
| TD
: Break, 250 µm | 55.0 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Yield, 250 µm | 4.0 | % | |
| TD
: Yield, 250 µm | 4.0 | % | |
| MD
: Break, 250 µm | 400 | % | |
| TD
: Break, 250 µm | 400 | % | |
| Ударное падение Dart 2 | | | ASTM D1709A |
| -18°C, 250 µm | 500 | g | |
| 23°C, 250 µm | 400 | g | |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 250 µm | 1400 | g | |
| TD
: 250 µm | 1700 | g | |
| Сопротивление разрыву брюк 3 | | | ISO 6383-1 |
| MD | 36.0 | N/mm | |
| TD | 36.0 | N/mm | |
| Проницаемость кислорода (23°C, 250 µm, 50% RH) | 10 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Скорость передачи водяного пара (38°C, 100% RH, 250 µm) | 7.0 | g/m²/24 hr | ASTM F1249 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 37 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -40°C | 4.2 | kJ/m² | ISO 180/1A |
| 23°C | 6.2 | kJ/m² | ISO 180/1A |
| Незубчатый изод Impact | | | |
| -40°C, 3.20 mm | No Break | | ASTM D4218 |
| -30°C, 3.20 mm | No Break | | ASTM D4218 |
| -20°C, 3.20 mm | No Break | | ASTM D4218 |
| 23°C, 3.20 mm | No Break | | ASTM D4218 |
| -40°C 4 | No Break | | ISO 180/1U |
| -30°C 5 | No Break | | ISO 180/1U |
| -20°C 6 | No Break | | ISO 180/1U |
| 23°C 7 | No Break | | ISO 180/1U |
| Ударное устройство для дротиков | | | |
| -40°C, 2.50 mm, Energy at Peak Load | 41.0 | J | ASTM D3763 |
| -40°C, 3.20 mm, Energy at Peak Load | 50.0 | J | ASTM D3763 |
| 23°C, 2.50 mm, Energy at Peak Load | 28.0 | J | ASTM D3763 |
| 23°C, 3.20 mm, Energy at Peak Load | 33.0 | J | ASTM D3763 |
| -40°C, 2.50 mm, Energy to Peak Force | 35.0 | J | ISO 6603-2 |
| -40°C, 3.20 mm, Energy to Peak Force | 36.0 | J | ISO 6603-2 |
| 23°C, 2.50 mm, Energy to Peak Force | 40.0 | J | ISO 6603-2 |
| 23°C, 3.20 mm, Energy to Peak Force | 44.0 | J | ISO 6603-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 64.0 | °C | |
| Температура перехода стекла | 80.0 | °C | DSC |
| Викат Температура размягчения | 85.0 | °C | ASTM D1525 |
| CLTE-
Поток (-30 to 40°C) | 5.1E-5 | cm/cm/°C | ASTM D696 |
| Удельный нагрев | | | DSC |
| 60°C | 1300 | J/kg/°C | |
| 100°C | 1760 | J/kg/°C | |
| 150°C | 1880 | J/kg/°C | |
| 200°C | 1970 | J/kg/°C | |
| 250°C | 2050 | J/kg/°C | |
| Теплопроводность (23°C) | 0.21 | W/m/K | ASTM C177 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Диэлектрическая прочность 8(23°C) | 16 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная | | | ASTM D150 |
| 23°C, 1 kHz | 2.60 | | |
| 23°C, 1 MHz | 2.40 | | |
| Коэффициент рассеивания | | | ASTM D150 |
| 23°C, 1 kHz | 5.0E-3 | | |
| 23°C, 1 MHz | 0.020 | | |
| Дуговое сопротивление | 158 | sec | ASTM D495 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 250 µm) | 108 | | ASTM D2457 |
| Коэффициент пропускания | | | ASTM D1003 |
| Total, 250 µm | 91.0 | % | |
| Regular, 250 µm | 89.0 | % | |
| Четкость (250 µm) | 85.0 | | ASTM D1746 |
| Haze (250 µm) | 0.80 | % | ASTM D1003 |
| Примечание |
|---|
| 1 . | Split Tear Method, 254 mm/min |
| 2 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 3 . | 200 mm/min |
| 4 . | 4 mm |
| 5 . | 4 mm |
| 6 . | 4 mm |
| 7 . | 4 mm |
| 8 . | 500 V/sec, Method A (Short-Time) |