Описание материалов:

Alcryn® ALR 7225 MPR has improved heat resistance over standard Alcryn grades and has an upper temperature limit of 136°C, while retaining at least 85% of original tensile properties. ALR 7225 is designed for the extrusion process, specifically Wire & Cable applications and should be considered where increased temperature resistance is required.

Главная Информация
Характеристики	Теплостойкость, высокая
Используется	Применение проводов и кабелей
Рейтинг агентства	ЕС 2002/96/ЕС (WEEE)
Соответствие RoHS	Соответствие RoHS
Формы	Частицы
Метод обработки	Экструзия

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	1.30	g/cm³	ASTM D792, ISO 1183

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore A)	82		ASTM D2240, ISO 868

Эластомеры	Номинальное значение	Единица измерения	Метод испытания
Tensile Stress (100% Strain)	4.85	MPa	ASTM D412, ISO 37
Tensile Stress (Yield)	9.64	MPa	ISO 37
Удлинение при растяжении (Break)	370	%	ASTM D412, ISO 37
Tear Strength ¹(24°C)	39.8	kN/m	ASTM D624
Комплект сжатия
24°C, 22 hr	32	%	ASTM D395B
70°C, 22 hr	73	%	ASTM D395B
24°C, 22 hr ²	32	%	ISO 815
70°C, 22 hr ³	73	%	ISO 815

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	7.3E+11	ohms	ASTM D257
Сопротивление громкости	4.4E+11	ohms·cm	ASTM D257
Диэлектрическая прочность (0.00191 mm)	0.45	kV/mm	ASTM D149

Дополнительная информация
The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48.Permanent Set (Tension), ASTM D412: 15%100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 277°F: 117%Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 277°F: 99%Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 277°F: 131%Viscosity, ASTM D3835, 300 s-1 at 374°F: 628 Pa*sTypical Processing Temperature: 350° FClash-Berg Stiffness Temperature, ASTM D1043, 10000 psi: -19° CVolume Change, After 7 days, 100°C, Water: 34%Volume Change, After 7 days, 24°C, Fuel B: 36%Volume Change, After 7 days, 100°C, ASTM #1 Oil: -7%Volume Change, After 7 days, 100°C, IRM 903 Oil: 28%Volume Change, After 4 days, 100°C, ASTM #2 Oil: 9%Weight Change, After 7 days, 100°C, Water: 25%Weight Change, After 7 days, 24°C, Fuel B: 18%Weight Change, After 7 days, 100°C, ASTM #1 Oil: -6%Weight Change, After 7 days, 100°C, IRM 903 Oil: 18%Weight Change, After 4 days, 100°C, ASTM #2 Oil: 6%

Дополнительная информация

The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48.Permanent Set (Tension), ASTM D412: 15%100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 277°F: 117%Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 277°F: 99%Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 277°F: 131%Viscosity, ASTM D3835, 300 s-1 at 374°F: 628 Pa*sTypical Processing Temperature: 350° FClash-Berg Stiffness Temperature, ASTM D1043, 10000 psi: -19° CVolume Change, After 7 days, 100°C, Water: 34%Volume Change, After 7 days, 24°C, Fuel B: 36%Volume Change, After 7 days, 100°C, ASTM #1 Oil: -7%Volume Change, After 7 days, 100°C, IRM 903 Oil: 28%Volume Change, After 4 days, 100°C, ASTM #2 Oil: 9%Weight Change, After 7 days, 100°C, Water: 25%Weight Change, After 7 days, 24°C, Fuel B: 18%Weight Change, After 7 days, 100°C, ASTM #1 Oil: -6%Weight Change, After 7 days, 100°C, IRM 903 Oil: 18%Weight Change, After 4 days, 100°C, ASTM #2 Oil: 6%

Примечание
1 .	C mould
2 .	Type B
3 .	Type B

Тип материала	Категория	Производитель
K-Prene HYFLEX HF 15	MPR	Technovinyl Polymers India Ltd.
K-Prene INSULATION EPR 5088	MPR	Technovinyl Polymers India Ltd.
K-Prene SHEATHING EPR 5067	MPR	Technovinyl Polymers India Ltd.
Alcryn® 1080 BK	MPR	Advanced Polymer Alloys
Alcryn® 2160 NC	MPR	Advanced Polymer Alloys
Alcryn® 2380 NC	MPR	Advanced Polymer Alloys

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

