LUVOCOM® 65-7712/GY

Категория	PP, Polypropylene Copolymer , PP Copolymer
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	G3Hz0i_LUVOCOM-65-7712-GY.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®65-7712/GY is a polypropylene copolymer (PP Copoly) material, which contains glass and carbon fiber reinforced materials. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 65-7712/GY are:

Conductivity

Electrostatic protection

Good stiffness

Главная Информация
Наполнитель/армирование	Армированные материалы из стекла и углеродного волокна
Характеристики	Проводящий Жесткий, хороший Защита от электростатического разряда Хорошая прочность
Внешний вид	Серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.06	g/cm³	ISO 1183
Формовочная усадка	0.20 - 0.60	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	8000	MPa	ISO 527-2
Tensile Stress (Break)	53.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	1.0	%	ISO 527-2
Флекторный модуль	6000	MPa	ISO 178
Флекторный стресс	75.0	MPa	ISO 178
Flexural Strain at Flexural Strength	1.4	%	ISO 178

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0E+2	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	14	kJ/m²	ISO 179/1eU

Инъекция	Номинальное значение	Единица измерения
Температура сушки	70.0 - 95.0	°C
Время сушки	2.0 - 4.0	hr
Рекомендуемая максимальная влажность	0.20	%
Задняя температура	220 - 250	°C
Средняя температура	220 - 250	°C
Передняя температура	230 - 250	°C
Температура сопла	220 - 250	°C
Температура обработки (расплава)	230 - 260	°C
Температура формы	40.0 - 80.0	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Talcoprene® 1030TC BIANCO280	PP Homopolymer	SO.F.TER. SPA
ADENE® O07MQE-00	PP Homopolymer	A.D. Compound S.p.A.
AGRIPLAS™ BF20H	PP, Unspecified	A. Schulman Inc.
RTP PP 40 GF UV	PP, Unspecified	RTP Company
ACCUTECH™ CP0436C20L1	PP Copolymer	ACLO Compounders Inc.
Petrotene® PP A3 G20 NTLA010 PH304	PP, Unspecified	Petropol Industry and Trade of Polymers LTDA

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

