- INTEGRAL™ 801
INTEGRAL™ 801
| Категория | PO, Polyolefin Adhesive Film , Polyolefin, Unspecified |
| Производитель | The Dow Chemical Company |
| Торговая марка | INTEGRAL™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
G2h0uO_INTEGRAL-801.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
INTEGRAL™ 801 Film provides adhesion between substrates such as ABS and polystyrene at low processing temperatures. This product should be considered where temperature-sensitive substrates such as synthetic fabrics
are involved.
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
are involved.
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
- Heat Activation Point: 160°F (71°C)
- Yield: 203 sq ft/lb/mil (41.5 m²/kg/25 µm)
- Available Colors: Clear
- Gauge Range: 1.0-2.0 mil (25-50 µm)
- Width Range: 20-66 in (508-1576 mm)
| Главная Информация | |
|---|---|
| Внешний вид |
|
| Формы |
|
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 51 | µm | |
| Толщина пленки-рекомендовано/доступно | 1.0-2.0 mil (25-50 µ) | ||
| Сектантный модуль | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 123 | MPa | |
| 2% Secant, TD : 51 µm | 131 | MPa | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Break, 51 µm | 24.5 | MPa | |
| TD : Break, 51 µm | 14.5 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 51 µm | 400 | % | |
| TD : Break, 51 µm | 650 | % | |
| Ударное падение Dart (51 µm) | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 190 | g | |
| TD : 51 µm | 340 | g | |
| Ширина пленки | 50.80 to 167.64 | cm | |
| Peel Strength 1 | Internal Method | ||
| to ABS | 669.7 | g/2.5 cm | |
| to HIPS | 982.2 | g/2.5 cm | |
| to Polystyrene | 759.0 | g/2.5 cm | |
| Выход (25,0 мкм) | 41.5 | m²/kg |
| Тепловой | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура активации тепла | 71 | °C |
| Примечание | |
|---|---|
| 1 . | Heat seal testing at 300°F (149°C), 30 psi, (0.21 MPa), 1 second dwell. |
| Тип материала | Категория | Производитель |
|---|---|---|
| Toppyl SP 2001 B | Polyolefin, Unspecified | LyondellBasell Industries |
| CALP 1100G-1 | Polyolefin, Unspecified | Lion Idemitsu Composites Co., Ltd. |
| Hax™ HFX 507 | Polyolefin, Unspecified | Fainplast Compounds S.r.l |
| Hifax CA1147A | Polyolefin, Unspecified | LyondellBasell Industries |
| Hifax DG 232 2693 | Polyolefin, Unspecified | LyondellBasell Industries |
| RheTech Thermoplastic Polyolefin FT3080-01 | Polyolefin, Unspecified | RheTech, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved