D/W 2000 is a skived PTFE (Polytetrafluoroethylene) film held to close tolerance on width and thickness. D/W 2000 conforms to ASTM D 3308 Type II as well as to SAE AMS 3662C.
D/W 2000 finds use in electrical applications where high temperature service rating and/or superior electrical properties are desired. This material is often used as a release film in the production of high temperature flex circuit materials as well as in the production of microwave circuit materials where it is seen as both a release film and a bonding film. D/W 2000 is an excellent release film for the molding of composite structures.
| Главная Информация | |
|---|
| Характеристики | - Хорошие электрические свойства
- Высокая термостойкость
|
| Используется | - Склеивание
- Электрическое/электронное применение
- Пленка
- Защитная пленка
|
| Рейтинг агентства | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| Толщина | 0.1 to 1016.0 | µm | |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| Идентификатор ядра | 7.62 | cm | |
| Максимальный диаметр рулона | 356 | mm | |
| Ширина | 305 to 1270 | mm | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение-
MD (Yield) | 20.7 | MPa | ASTM D882 |
| Растяжимое удлинение-
MD (Break) | 330 | % | ASTM D882 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Температура непрерывного использования | 260 | °C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Диэлектрическая прочность | 79 | kV/mm | ASTM D149 |