Описание материалов:
Menzolit® BMC 0390 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® BMC 0390 is a low profile DMC/BMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surface quality is necessary that cannot be achieved with low shrink material. Because of the low shrinkage, tool design is more difficult and the user should take care to allow proper part ejection from mould. Typical applications are housings or covers that call for improved surface quality and dimensional stability. Because of this painting may be desired. Paint adhesion of appropriate paint systems is very good. Chrome plating of punch and cavity surfaces is recommended.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 25% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая адгезия
- Хорошая стабильность размеров
- Хорошая поверхность
- Без галогенов
- Высокая термостойкость
- Низкая усадка
- Низкий уровень дыма
- Низкий уровень защиты
|
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.030 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 36.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 11000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 120 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 30 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 165 | °C | Internal Method |
| Температура перехода стекла | 170 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Температура зажигания провода свечения | 750 | °C | IEC 60695-2-13 |
| Индекс кислорода | 22 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Glow Bar | Level BH 2 <= 95 | | IEC 60707-3 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |