Описание материалов:

LUVOCOM®50-9022 is a polycarbonate (PC) material,. This product is available in Europe,.

LUVOCOM®The main features of 50-9022 are:

Good dimensional stability

Impact resistance

Wear-resistant

Lubrication

Typical application areas include:

engineering/industrial accessories

Electrical/electronic applications

Reflector

business/office supplies

Sporting goods

Главная Информация
Добавка	Ptfe лубрикант
Характеристики	Хорошая стабильность размеров Низкий коэффициент трения Хорошая ударопрочность Хорошая стойкость к истиранию Смазка
Используется	Шестерня Зеркало Инженерные аксессуары Переключатель Бизнес-оборудование Спортивные товары Медицинские принадлежности/принадлежности для ухода
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.25	g/cm³	ISO 1183
Массовый расход расплава (MFR) (300°C/5.0 kg)	45	g/10 min	ISO 1133
Плавкий объем-расход (MVR) (300°C/5.0 kg)	40.0	cm³/10min	ISO 1133
Формовочная усадка	0.60 - 0.80	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.20	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	2300	MPa	ISO 527-2
Tensile Stress (Break)	54.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.8	%	ISO 527-2
Флекторный модуль	2000	MPa	ISO 178
Флекторный стресс	78.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Ударная прочность			ISO 179/1eA
-30°C	15	kJ/m²	ISO 179/1eA
23°C	25	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength
-30°C	80	kJ/m²	ISO 179/1fU
23°C	180	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	132	°C	ISO 75-2/A
Температура непрерывного использования	130	°C	UL 746B
Викат Температура размягчения	160	°C	ISO 306/A
CLTE- Поток	7.0E-5	cm/cm/°C	DIN 53752

Инъекция	Номинальное значение	Единица измерения
Температура сушки	120	°C
Время сушки	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	280 - 300	°C
Средняя температура	290 - 310	°C
Передняя температура	300 - 320	°C
Температура сопла	290 - 310	°C
Температура обработки (расплава)	295	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
NEXUS PC PC1212FRR	PC	Nexus Resin Group, LLC.
LNP™ LUBRICOMP™ DFP34 compound	PC	SABIC Innovative Plastics
LEXAN™ ML6411 resin	PC	SABIC Innovative Plastics Europe
ALCOM® PC 740/4 GY1152-05LD	PC	ALBIS PLASTIC GmbH
LEXAN™ PC1000R resin	PC	SABIC Innovative Plastics
LEXAN™ CFR9131 resin	PC	SABIC Innovative Plastics

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

