Описание материалов:
NYCOA 2237 is Nylon copolymer resin that exhibits excellent transparency and good barrier properties. The resin was developed especially for applications requiring transparency in thickness up to 5 mm, while retaining the properties and chemical resistanc
NYCOA 2237 has been specifically designed to offer easy processability. It can be processed on conventional extrusion and injection equipment designed to process standard grades of nylon.
NYCOA 2237 is available with custom additive packages: heat stabilizer and/or UV stabilizer.
Typical injection molding applications include sight glasses, chemical splash goggles, fashion eyeglass frame, high-voltage switch casings, filter housings, pump casings, flow meters, liquid-level indicators, and filter bowls for gas.
Typical extrusion applications include high-end transparent fishing lines, tubing, transparent sheets, and decorative films for sports and automotive applications.
| Главная Информация | |
|---|
| Характеристики | - Сополимер
- Обрабатываемость, хорошая
- Хорошая химическая стойкость
- Высокое разрешение
- Барьерная смола
|
| Используется | - Оборудование для безопасности
- Пленка
- Мононити
- Электрический корпус
- Фитинги для труб
- Рамка
- Лист
- Применение в автомобильной области
- Спортивные товары
- Чехол
- Очки
- Применение рыболовства
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.12 | g/cm³ | ASTM D792 |
| Формовочная усадка | | | ASTM D955 |
| Flow | 1.0 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Поглощение воды (24 hr) | 1.7 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 60 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение 1 | 75.0 | MPa | ASTM D638 |
| Удлинение при растяжении 2(Break) | 100 | % | ASTM D638 |
| Флекторный модуль 3 | 2200 | MPa | ASTM D790 |
| Flexural Strength 4 | 90.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (6.35 mm) | 69 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Температура плавления | 199 | °C | |
| Дополнительная информация |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.1 | °C | |
| Время сушки | 4.0 - 6.0 | hr | |
| Задняя температура | 204 - 216 | °C | |
| Средняя температура | 216 - 227 | °C | |
| Передняя температура | 221 - 232 | °C | |
| Температура сопла | 221 - 238 | °C | |
| Температура обработки (расплава) | 216 - 232 | °C | |
| Температура формы | 4.44 - 10.0 | °C | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Подушка | 1.59 - 6.35 | mm | |
| Отношение винта L/D | 18.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Примечание |
|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |