Braskem PE STN7006

Категория	LDPE, Low Density Polyethylene
Производитель	Braskem America Inc.
Торговая марка	Braskem PE
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	Ee1HFZ_Braskem-PE-STN7006.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Description: STN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866.

Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness.

Process: Blown Film Extrusion

Главная Информация
Характеристики	Низкоскоростная затвердевающая точка Оптическая производительность Обновляемые ресурсы Высокое разрешение Без BPA Без добавления присадок
Используется	Ламинат Литая пленка Бутылка Пищевая упаковка
Рейтинг агентства	Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
Метод обработки	Экструзионная пленка Выдувная пленка

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	0.924	g/cm³	ASTM D792
Массовый расход расплава (MFR) (190°C/2.16 kg)	0.60	g/10 min	ASTM D1238

Пленки	Номинальное значение	Единица измерения	Метод испытания
Толщина пленки протестирована	50	µm
Сектантный модуль			ASTM D882
2% secant, MD : 50 µm, blown film	140	MPa	ASTM D882
2% secant, TD : 50 µm, blown film	170	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Broken, 50 µm, blown film	25.0	MPa	ASTM D882
TD : Broken, 50 µm, blown film	20.0	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Broken, 50 µm, blown film	350	%	ASTM D882
TD : Broken, 50 µm, blown film	700	%	ASTM D882
Ударное падение Dart ¹(50 µm, Blown Film)	170	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm, blown film	310	g	ASTM D1922
TD : 50 µm, blown film	250	g	ASTM D1922

Оптический	Номинальное значение	Единица измерения	Метод испытания
Блеск			ASTM D2457
45, blown film	60		ASTM D2457
60, blown film	86		ASTM D2457
Haze (Blown Film)	8.5	%	ASTM D1003

Дополнительная информация	Номинальное значение	Единица измерения	Метод испытания
Двуслойное содержание	> 95	%	ASTM D6866
Blown Film Properties: 50µm thickness film, processed in a 50mm blow film line with barrier screw. 25:1 L/D and a 1.0mm die gap at a 2.3:1 blow up ratio.Recommended processing conditions:Blow Film ExtrusionTemperature Profile:……....from 150 to 185°CMass Temperature:........... from 180 to 185°CBlow up Ratio:…………….….from 2,0 to 3,0:1Die Gap:………………………..1,0 mm

Примечание
1 .	F50

Тип материала	Категория	Производитель
DOW™ LDPE 352E	LDPE	The Dow Chemical Company
COSMOTHENE® L705	LDPE	TPC, The Polyolefin Company (Singapore) Pte Ltd
Epolene® C-23	LDPE	Westlake Chemical Corporation
Hanwha Total PE 620L	LDPE	HANWHA TOTAL PETROCHEMICALS Co., Ltd.
Petrothene® NA985	LDPE	LyondellBasell Industries
SABIC® LDPE 1808AN00	LDPE	Saudi Basic Industries Corporation (SABIC)

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

