TOTAL Polyethylene Lumicene® M 5510 EP
Описание материалов:
Lumicene® mPE M5510 EP is a second generation metallocene high density homopolymer Polyethylene.
Lumicene® mPE M5510 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The outstanding stiffness combined with good optical properties brings a significant down-gauging potential.
The high density of Lumicene® mPE M5510 EP enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE.
Lumicene® mPE M5510 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, heavy-duty sacks, automatic packaging specialty film, mailing film and lamination.
| Главная Информация | |
|---|
| Добавка | - Вспомогательные средства для обработки
- Устойчивость к окислению
|
| Характеристики | - Жесткий, хороший
- Высокая плотность
- Оптическая производительность
- Гомополимер
- Устойчивость к окислению
- Соответствие пищевого контакта
|
| Используется | - Упаковка
- Пленка
- Ламинат
- Сумка
- Тяжелая упаковочная сумка
|
| Рейтинг агентства | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.955 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 40 | µm | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 40 µm, blown film | 27.5 | MPa | ISO 527-3 |
| TD
: Yield, 40 µm, blown film | 28.0 | MPa | ISO 527-3 |
| MD
: Broken, 40 µm, blown film | 57.0 | MPa | ISO 527-3 |
| TD
: Broken, 40 µm, blown film | 45.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Broken, 40 µm, blown film | 870 | % | ISO 527-3 |
| TD
: Broken, 40 µm, blown film | 910 | % | ISO 527-3 |
| Тест на падение Dart-
Выдувная пленка
(40,0 мкм) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 40.0 µm | 11.0 | kN/m | ISO 6383-2 |
| TD
: 40.0 µm | 90.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 133 | °C | ISO 306 |
| Температура плавления | 134 | °C | ISO 11357-3 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 40.0 µm, Blown Film) | 40 | | ASTM D2457 |
| Haze (40.0 µm, Blown Film) | 24 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 200 - 230 | °C | |
| Инструкции по экструзии |
|---|
| BUR: 1.5:1 to 4.5:1Die Gap: 0.8 to 2.8 mm |