CONTINUUM™ DGDC-2482 NT

Категория HDPE, Bimodal Polyethylene Resin
Производитель The Dow Chemical Company
Торговая марка CONTINUUM™
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF ELagcg_CONTINUUM-DGDC-2482-NT.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
CONTINUUM™ DGDC-2482 NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation are desired. Suitable applications include natural gas distribution pipes, large diameter industrial piping, mining, sewage, and municipal water service lines.

Industrial Standards Compliance:
ASTM D 3350: cell classification
  • Natural - PE445574A
  • Black - PE445574C (See NOTES 1)
Plastics Pipe Institute (PPI): TR-4
  • Black Pipe - CONTINUUM DGDC-2482 BK (See NOTES 1)
    • ASTM PE4710 pipe grade - 1600psi HDB @ 73°F and 1000psi HDB @ 140°F
NSF International: Standard 14 and 61
  • Black Pipe - DGDC-2482 BK (See NOTES 1)
Consult the regulations for complete details.

NOTES:
(1) Natural resin extruded under proper conditions with Dow-approved carbon black masterbatch (6.5%).
Главная Информация
Добавка
  • Обработка помощи
Рейтинг агентства
  • Астм д 3350 PE445574A
  • Астм д 3350 PE445574C
  • ASTM PE4710
  • Утверждено NSF 14
  • Утверждено NSF 61
  • PPI TR-4
Формы
  • Гранулы
Метод обработки
  • Экструзионный профиль
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес ASTM D792
    Natural 0.949g/cm³
    Black 10.959g/cm³
Массовый расход расплава (MFR) ASTM D1238
    190°C/2.16 kg 0.080g/10 min
    190°C/21.6 kg 6.8g/10 min
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Прочность на растяжение 2(Yield)> 24.1MPaASTM D638
Удлинение при растяжении 3(Break)> 500%ASTM D638
Флекторный модуль 1030MPaASTM D790B
Гидростатическая прочность 4ASTM D1598
    1798 psi (12.4 MPa) : 20°C > 100hr
    798 psi (5.5 MPa) : 80°C > 1000hr
Устойчивость к быстрому размножению трещин, ПК 5> 12.0barISO 13477
Устойчивость к быстрому размножению трещин, Tc 6< -17°CISO 13477
Медленная трещина роста 7> 5000hrASTM F1473
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Термическая стабильность > 220°CASTM D3350
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Зубчатый изод Impact 8(23°C)490J/mASTM D256A
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура ломкости 9< -75.0°CASTM D746A
Примечание
1 .Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)
2 .Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time.
3 .Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time.
4 .Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)
5 .3Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11.
6 .3Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11.
7 .Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time.
8 .Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time.
9 .Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time.
Тип материала Категория Производитель
Premier HD11051 HDPE Premier Polymers, LLC.
PRIMALENE WPP702 HDPE Southern Polymer, Inc.
SABIC® Vestolen A 5061R 65308 HDPE Saudi Basic Industries Corporation (SABIC)
VENELENE® 7000F HDPE Poliolefinas Internacionales, C.A. (Polinter)
Evolue™-H SP6505 HDPE Prime Polymer Co., Ltd.
Kemcor HD 1155 HDPE, HMW Qenos Pty Ltd
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами