FireCon™ CPE 30-33 RoHS BLACK
Описание материалов:
The filled flexible thermoplastic CPE sheath compound material is a good choice for low-voltage power and cable control cables. Wire and cable manufacturers can use products for thermoplastic extrusion processing without investing in continuous vulcanization (CV) equipment. CPE 37-11 has been improved in terms of elasticity and ductility, while the brittleness has also been reduced, and it feels more rubber to touch. This combination material can replace thermosetting CPE materials in power, control cables and other applications.
| Главная Информация | |
|---|
| Используется | - Кабельная оболочка
- Применение проводов и кабелей
|
| Соответствие RoHS | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.31 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/21.6 kg) | 15 | g/10 min | ASTM D1238 |
| Внешний вид | Particles/cubes | | ASTM D2090 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 39 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение 1(Break) | 11.0 | MPa | ASTM D638 |
| Удлинение при растяжении 2(Break) | 450 | % | ASTM D638 |
| Флекторный модуль 3 | 6.41 | MPa | ASTM D790 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | -33.0 | °C | ASTM D746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс кислорода (1.91 mm) | 30 | % | ASTM D2863 |
| Дополнительная информация |
|---|
| 注释：推荐的预干燥为在175°-185°F环境下4小时。注释：根据螺旋设计不同，典型加工温度处于320° - 390°F之间。请联系技术服务部，获取特定设备的推荐。注释：模制厚板的典型属性（0.075"）；不能视为技术规格。 |
| Примечание |
|---|
| 1 . | Type 4, 510mm/min |
| 2 . | Type 4, 510mm/min |
| 3 . | 13 mm/min |