Techsil RTV2420
| Категория | Silicone |
| Производитель | Techsil Limited |
| Торговая марка | Techsil |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
Dy7gO3_Techsil-RTV2420.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
This is a two component room temperature condensation curing silicone compound. The cured product is an exceptionally flexible rubber with very high mechanical properties and good shelf life stability. It is suitable for mould making of intricate patterns with extremely good pick up of fine details. Softer grades are better suited for use where there are deep undercuts.
Key Features
Key Features
- High tear strength
- High detail pick up
- Easy degassing
- Good dimensional stability
| Главная Информация | |
|---|---|
| Характеристики |
|
| Внешний вид |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 1.26 | g/cm³ | BS 903 |
| Формовочная усадка- Поток | 4.0 | % |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Твердость дюрометра (Shore A) | 22 | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 0.930 | MPa | BS 903 |
| Прочность на растяжение 2(Yield) | 3.64 | MPa | BS 903 |
| Удлинение при растяжении 3(Break) | 500 | % | BS 903 |
| Tear Strength 4 | 26.2 | kN/m | BS 903 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|---|---|---|
| CLTE | |||
| Flow | 2.5E-4 | cm/cm/°C | |
| Transverse | 7.4E-4 | cm/cm/°C | |
| Service Temperature 5 | -50 to 200 | °C |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Модуль Young's 6 | 1.50 | MPa |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Срок службы горшка 7 | 75 | min | |
| Терморегулирующая вязкость | |||
| -- 8 | 19000 | cP | |
| -- 9 | 25000 | cP | |
| Время демолд 10 | 480 | min |
| Примечание | |
|---|---|
| 1 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 2 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 3 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 4 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 5 . | AFS 1540B |
| 6 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 7 . | measured at 23+/-2°C and 65% relative humidity using standard catalyst |
| 8 . | Catalysed, Brookfield |
| 9 . | Brooksfield |
| 10 . | measured at 23+/-2°C and 65% relative humidity using standard catalyst |
| Тип материала | Категория | Производитель |
|---|---|---|
| NuSil MED-6670 | Silicone | NuSil Technology |
| Generic Silicone - Unspecified | Silicone | Generic |
| Precision Polymer S80U | Silicone | Precision Polymer Engineering Ltd. |
| NuSil MED-6019 | Silicone | NuSil Technology |
| Shin-Etsu Elastomer KE-1950-70A/B | Silicone Rubber, HTV | Shin-Etsu Silicones of America |
| Silastic® Medical Adhesive Silicone, Type A | Silicone | Dow Corning Corporation |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved