Описание материалов:
APTIV® 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications.
APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.
APTIV 1000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users.
| Главная Информация | |
|---|
| Характеристики | - Барьерная смола
- Чистота/Высокая чистота
- Прочный
- Электрически изолирующий
- Отличная Печатающая способность
- Огнестойкий
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Хорошая износостойкость
- Без галогенов
- Термогерметичный
- Высокая термостойкость
- Высокая прочность
- Устойчивость к гидролизу
- Низкое поглощение влаги
- Низкий уровень дыма
- Низкая токсичность
- Металлизируемый
- Устойчивость к излучению (гамма)
- Перерабатываемый материал
- Полукристаллический
- Свариваемый
|
| Используется | - Аэрокосмическое применение
- Уплотнение
- Диафрагмы
- Электрическое/электронное применение
- Пленка
- Изоляция
- Этикетки
- Ламинаты
- Мембраны
- Печатные платы
- Лента
- Шайба
|
| Рейтинг агентства | - ЕС 2002/72/ЕС
- ЕС 2004/19/ЕС
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,2415
|
| Соответствие RoHS | |
| Формы | |
| Метод обработки | - Покрытие
- Ламинирование
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Поглощение воды 1(Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.040 | % | ISO 62 |
| Усадка (200 °C, 50,0 мкм) 2 | < 2.0 | % | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Dielectric Breakdown | | | ASTM D149 |
| 23°C, 25.0 µm | 6750 | V | |
| 23°C, 50.0 µm | 9500 | V | |
| 23°C, 125.0 µm | 15000 | V | |
| 23°C, 250.0 µm | 17500 | V | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление проколу (23 °C, 50,0 мкм) | 26.0 | kJ/m² | Internal Method |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки-рекомендовано/доступно | 8 to 750 µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 23°C, 25 µm | 3000 | MPa | |
| 23°C, 50 µm | 2800 | MPa | |
| 23°C, 130 µm | 2400 | MPa | |
| 23°C, 250 µm | 2200 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| Break, 23°C, 25 µm | 130 | MPa | |
| Break, 23°C, 50 µm | 120 | MPa | |
| Break, 23°C, 130 µm | 110 | MPa | |
| Break, 23°C, 250 µm | 100 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| Break, 23°C, 25 µm | > 150 | % | |
| Break, 23°C, 50 µm | > 150 | % | |
| Break, 23°C, 130 µm | > 150 | % | |
| Break, 23°C, 250 µm | > 150 | % | |
| Сопротивление разрыву брюк 3(50 µm) | 6.70 | N/mm | ISO 6383-1 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток 4(0.0500 mm) | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости 5(23°C, 0.0500 mm) | 4.0E+16 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность | | | ASTM D149 |
| 23°C, 0.0250 mm | 270 | kV/mm | |
| 23°C, 0.0500 mm 6 | 190 | kV/mm | |
| 23°C, 0.125 mm | 120 | kV/mm | |
| 23°C, 0.250 mm | 70 | kV/mm | |
| Диэлектрическая постоянная (23°C, 0.0500 mm, 10 MHz) | 3.50 | | ASTM D150 |
| Коэффициент рассеивания (23°C, 0.0500 mm, 10 MHz) | 2.0E-3 | | ASTM D150 |
| Примечание |
|---|
| 1 . | 24 hrs |
| 2 . | TM-VX-84 |
| 3 . | 23°C |
| 4 . | below Tg |
| 5 . | 100 V |
| 6 . | 0.25 inch electrode |