Описание материалов:
By selecting specific monomers, one can achieve a crystallizable and permanently transparent polyamide: TROGAMID® CX. The crystallites are so small that they do not scatter visible light, and the material appears transparent to the human eye—a property known as microcrystallinity. Because of its crystallinity, the microcrystalline structure retains important properties such as stress cracking resistance — without clouding. The degree of crystallinity is so negligible, however, that it has no adverse effect on the shrinkage behavior of molded parts. TROGAMID® CX undergoes a similar isotropic shrinkage like amorphous materials.
The combination of good UV resistance, high mechanical strength, permanent transparency, high transmission and superior chemical resistance opens a wide range of applications for TROGAMID® CX. Typical areas of application are in the automotive industry, machinery and engineering, medical technology, the sports and recreation industry, the glasses production, the cosmetics industry and in water treatment and filter technology.
TROGAMID® CX9701:
High-viscous, permanently transparent polyamide for extrusion, with an external feeding aid
| Главная Информация | |
|---|
| Характеристики | - Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая стабильность размеров
- Хорошая технологичность
- Хорошая устойчивость к ультрафиолетовому излучению
- Высокий уровень ЭСКП (устойчивость к стрессу)
- Высокая ударопрочность
- Высокая вязкость
- Низкая усадка
- Ударопрочность при низкой температуре
- Низкое поглощение воды
- Устойчивость к царапинам
|
| Используется | - Автомобильные Приложения
- Косметика
- Инженерные приложения
- Фильтры
- Оптическое применение
- Спортивные товары
|
| Внешний вид | - Прозрачный/прозрачный
- Доступные цвета
- Натуральный цвет
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Номер вязкости | 180 to 200 | cm³/g | ISO 307 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше (Shore D) | 81 | | ISO 868 |
| Твердость мяча | 110 | MPa | ISO 2039-1 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ISO 527-2 |
| 23°C | 1500 | MPa | |
| 80°C | 1270 | MPa | |
| Tensile Stress | | | ISO 527-2/50 |
| Yield, 23°C | 60.0 | MPa | |
| Yield, 80°C | 48.0 | MPa | |
| Растяжимое напряжение | | | ISO 527-2/50 |
| Yield, 23°C | 8.0 | % | |
| Yield, 80°C | 5.5 | % | |
| Номинальное растяжение при разрыве | | | ISO 527-2/50 |
| 23°C | > 50 | % | |
| 80°C | > 50 | % | |
| Растяжимый ползучий модуль | | | ISO 899-1 |
| 1 hr | 1400 | MPa | |
| 1000 hr | 700 | MPa | |
| Флекторный модуль | 1700 | MPa | ISO 178 |
| Флекторный стресс 1 | | | ISO 178 |
| 3.5% Strain | 50.0 | MPa | |
| -- | 90.0 | MPa | |
| Outer Fiber Strain -
at maximum stress 2 | 9.0 | % | ISO 178 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс температуры 3 | 100 | °C | IEC 216 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| -30°C, Complete Break | 14 | kJ/m² | |
| 0°C, Complete Break | 15 | kJ/m² | |
| 23°C, Complete Break | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | ISO 179/1eU |
| -30°C | No Break | | |
| 0°C | No Break | | |
| 23°C | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 108 | °C | ISO 75-2/A |
| Температура перехода стекла 4 | 140 | °C | ISO 11357-2 |
| Викат Температура размягчения | | | |
| -- | 137 | °C | ISO 306/A |
| -- | 130 | °C | ISO 306/B |
| Температура плавления (DSC) 5 | 250 | °C | DSC |
| CLTE | | | ISO 11359-2 |
| Flow
: 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Transverse
: 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+13 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+16 | ohms·cm | IEC 60093 |
| Электрическая прочность | 27 | kV/mm | IEC 60243-1 |
| Относительная проницаемость | | | IEC 60250 |
| 23°C, 100 Hz | 3.60 | | |
| 23°C, 1 MHz | 3.20 | | |
| Коэффициент рассеивания | | | IEC 60250 |
| 23°C, 100 Hz | 0.012 | | |
| 23°C, 1 MHz | 0.033 | | |
| Comparative Tracking Index | | | IEC 60112 |
| -- 6 | 575 | V | |
| Solution A | 600 | V | |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 0.800 mm | HB | | |
| 1.60 mm | HB | | |
| Индекс воспламеняемости провода свечения (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Температура зажигания провода свечения (1.00 mm) | 800 | °C | IEC 60695-2-13 |
| Примечание |
|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | Criterion: stress at yield |
| 4 . | 10 K/min |
| 5 . | 2nd Heating |
| 6 . | 100 drops value |