Описание материалов:
The Petrothene GA601 series resins are pelletized linear low density polyethylenes selected by customers for applications that require maximum strength and toughness. These products offer excellent additive homogeneity, require no transfer equipment modification, and facilitate clean and safe handling. Typical applications include heavy duty shipping sacks, trash can liners, commercial and industrial packaging, as well as food and consumer packaging. The GA601 series resins offer enhanced film strength, drawdown, toughness and heat seal strength. In addition, these resins have excellent low temperature resistance for applications such as stretch film and frozen food packaging. The GA601 series resins can be purchased without additives or fully formulated with slip and antiblock.
| Главная Информация | |
|---|
| Добавка | - Антиблок (6500 ppm)
- Скольжения (1350 ppm)
|
| Характеристики | - Антиблокировка
- Приемлемый пищевой контакт
- Хорошая просадка
- Хорошее тепловое уплотнение
- Хорошая прочность
- Хорошая прочность
- Комбинация
|
| Используется | - Сумки
- Пленка
- Пищевая упаковка
- Промышленное применение
- Вкладыши
- Упаковка
- Эластичная пленка
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.918 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль | | | ASTM D882 |
| 1% Secant, MD
: 25 µm | 200 | MPa | |
| 1% Secant, TD
: 25 µm | 224 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Break, 25 µm | 55.8 | MPa | |
| TD
: Break, 25 µm | 42.1 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 25 µm | 580 | % | |
| TD
: Break, 25 µm | 700 | % | |
| Ударное падение Dart (25 µm, Blown Film) | 190 | g | ASTM D1709A |
| Общее воздействие энергии (25 µm, Blown Film) | 2.44 | J | ASTM D4272 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm | 330 | g | |
| TD
: 25 µm | 650 | g | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 105 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 25.4 µm, Blown Film) | 35 | | ASTM D2457 |
| Haze (25.4 µm, Blown Film) | 22 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 204 to 232 | °C | |