Описание материалов:
XH-03A CHLORINATED POLYETHYLENE (CPE) COMPOUND FOR 65°C HEAVY FLAME-RESISTANT RUBBER JACKET
PRODUCT FEATURES:
Our company can manufacture XH-03A CPE jacket material through many experiments and tests. After continuous curing, all properties of this rubber cable jacket can meet and surpass the Standard No. GB7594.5.
MAIN APPLICATION:
This product can be used to manufacture heavy cable jacket which its conductor allowable work-temperature can stay at 65 for a long trem. It has excellent tenacity, oil-resistance, heat-resistance, ozone resistance and fine flame resistance, it also can subsititute CR rubber compound completely. The manufactured cable, particularly suitable for the long-term poor working conditions. Our red and yellow mineral cable jacket material can satisfy the Standard No. GB12972-91.
| Главная Информация | |
|---|
| Характеристики | - Огнестойкий
- Высокая термостойкость
- Маслостойкий
- Устойчивость к озону
|
| Используется | |
| Эластомеры | Номинальное значение | Единица измерения | |
|---|
| Tensile Stress 1(Break) | > 11.0 | MPa | |
| Удлинение при растяжении | | | |
| Break 2 | > 250 | % | |
| Break 3 | > 300 | % | |
| Старение | Номинальное значение | Единица измерения | |
|---|
| Изменение напряжения при растяжении | | | |
| 75°C, 240 hr, in Air oven | -15 to 15 | % | |
| 100°C, 24 hr, in IRM 902 Oil | -40 to 40 | % | |
| Изменение натяжения при разрыве | | | |
| 75°C, 240 hr, in Air oven | -25 to 25 | % | |
| 100°C, 24 hr, in IRM 902 Oil | -40 to 40 | % | |
| Воспламеняемость | Номинальное значение | Единица измерения | |
|---|
| Индекс кислорода | > 35 | % | |
| Примечание |
|---|
| 1 . | Before ageing test |
| 2 . | After Oven ageing test |
| 3 . | Before ageing test |