Cereplast Compostables® 1006
Описание материалов:
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments.
All Cereplast Compostables® resins, including Compostable 1006, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432).
Compostable 1006 has been designed to have an excellent balance of high stiffness, toughness, and processability. Compostable 1006 can be processed on existing conventional electric and hydraulic reciprocating screw injection molding machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, хороший
- Compostable
- Обновляемые ресурсы
- Обрабатываемость, хорошая
- Хорошая прочность
- Биоразлагаемый
|
| Рейтинг агентства | - ASTM D 6400
- ASTM D 6868
- RU 13432
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.36 | g/cm³ | ASTM D792A |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 5100 | MPa | ASTM D638 |
| Прочность на растяжение (Break) | 55.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 4.0 | % | ASTM D638 |
| Флекторный модуль | 4930 | MPa | ASTM D790 |
| Flexural Strength | 90.3 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (23°C) | 33 | J/m | ASTM D256 |
| Ударное падение Dart | 1.13 | J | ASTM D5420 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (0.45 MPa, Unannealed) | 49.4 | °C | ASTM D648 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.1 - 82.2 | °C | |
| Время сушки | 2.0 - 4.0 | hr | |
| Задняя температура | 163 - 177 | °C | |
| Средняя температура | 177 - 191 | °C | |
| Передняя температура | 177 - 204 | °C | |
| Температура сопла | 177 - 204 | °C | |
| Температура обработки (расплава) | 174 - 204 | °C | |
| Температура формы | 10.0 - 26.7 | °C | |
| Screw Speed | 50 - 100 | rpm | |
| Инструкции по впрыску |
|---|
| Material Drying Temp (regrind): 100 to120°F (4 hrs.) |