Описание материалов:
Lyondellbasell Australia's polypropylene grade HP401H is a low flow homopolymer with a conventional molecular weight distribution and is formulated with a general purpose additive package. HP401H is designed principally for the production of sheet for subsequent forming operations into packaging containers. The flow level has been chosen to provide a good balance between hot melt strength during processing and high production rates. Sheet and formed containers produced from HP401H exhibit an attractive balance of rigidity, clarity and impact performance.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая ударопрочность
- Хорошая прочность расплава
- Хорошая технологичность
- Хорошая жесткость
- Гомополимер
- Низкий поток
|
| Используется | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.900 | g/cm³ | ISO 1183/D |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше (Shore D) | 73 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2 |
| Флекторный модуль | 1400 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод ударная прочность (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, Unannealed | 82.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 51.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | 155 | °C | ISO 306 |