Описание материалов:
Eastar™ Copolyester MN211 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. Eastar™ copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. MN211 contains a mold release.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Стерилизуемый e-луч
- Хорошая химическая стойкость
- Хорошая стабильность цвета
- Хорошая стабильность размеров
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Высокая четкость
- Низкая усадка
- Радиационный стерилизуемый
|
| Используется | - Медицинские/медицинские приложения
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.27 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Поглощение воды (23°C, 24 hr) | 0.13 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 106 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| Yield, 23°C | 50.0 | MPa | |
| Break, 23°C | 28.0 | MPa | |
| Удлинение при растяжении | | | ASTM D638 |
| Yield, 23°C | 4.3 | % | |
| Break, 23°C | 110 | % | |
| Флекторный модуль (23°C) | 2100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 70.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C | 37 | J/m | |
| 23°C | 100 | J/m | |
| Незубчатый изод Impact | | | ASTM D4218 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 63.0 | °C | |
| Викат Температура размягчения | 85.0 | °C | ASTM D1525 |
| Удельный нагрев | | | ASTM D2766 |
| 60°C | 1300 | J/kg/°C | |
| 240°C | 2010 | J/kg/°C | |
| Теплопроводность (23°C) | 0.19 | W/m/K | |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания | | | ASTM D1003 |
| Total | 91.0 | % | |
| Regular | 88.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.0 | °C | |
| Время сушки | 4.0 to 6.0 | hr | |
| Температура обработки (расплава) | 249 to 271 | °C | |
| Температура формы | 16.0 to 38.0 | °C | |