Andur M-11 (94% 1,4BD, 6% TMP)
Описание материалов:
Andur M-11 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 92 | | ASTM D2240 |
| Shaw D | 42 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.689 | MPa | ASTM D695 |
| 5% strain | 1.72 | MPa | ASTM D695 |
| 10% strain | 3.45 | MPa | ASTM D695 |
| 15% strain | 4.83 | MPa | ASTM D695 |
| 20% strain | 6.21 | MPa | ASTM D695 |
| 25% strain | 7.93 | MPa | ASTM D695 |
| 50% strain | 29.0 | MPa | ASTM D695 |
| Устойчивость к истиранию | 50.3 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 7.93 | MPa | ASTM D412 |
| 200% strain | 17.2 | MPa | ASTM D412 |
| 300% strain | 27.6 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 42.1 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 410 | % | ASTM D412 |
| Комплект сжатия | 30 | % | ASTM D395 |
| Сопротивляемость Bayshore | 28 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 8.0 | min | |
| Время демолд | 35 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 660 pliAverage Split Tear, ASTM D1938: 235 pliStoichiometry Curative Level: 95%NBS Abrasion: 220% Rubber StandardParts of curative per 100 parts Andur M-11, 8.9% NCO: 9.08 parts by weightParts of curative per 100 parts Andur M-11, 9% NCO: 9.18 parts by weightParts of curative per 100 parts Andur M-11, 9.1% NCO: 9.28 parts by weightParts of curative per 100 parts Andur M-11, 9.2% NCO: 9.39 parts by weightMix Temperature:
Andur M-11: 176-194°F
Curative 1,4BD/TMP: 77-158°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 90.0 - 120 | °C | |