DOW™ LDPE 320E
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
AKB6kF_DOW-LDPE-320E.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOW LDPE 320E is a low melt index, low density polyethylene resin. DOW LDPE 320E is specially developed for high transparency and gloss. The improved optical properties can also be seen in LLDPE blends, especially in structures with high LDPE content. Due to its excellent drafting performance, it can be used for processing some thinner structural parts.
application field:
composite film for food packaging, display packaging and consumer goods packaging
main characteristics:
DOW LDPE 320E should meet the requirements of the following regulations:
slip agent content: 0 ppm
opening agent content: 0 ppm
application field:
composite film for food packaging, display packaging and consumer goods packaging
main characteristics:
- Excellent processability and drafting performance
- Used in applications that require excellent optical properties, it can be used alone or blended with LLDPE
DOW LDPE 320E should meet the requirements of the following regulations:
- U.S. Food and Drug Administration Regulation 21 CFR 177.1520 (c) 2.2
- EU, No 10/2011
slip agent content: 0 ppm
opening agent content: 0 ppm
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.925 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения | 0.50 - 0.70 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Энергия прокола пленки (50 µm) | 1.70 | J | Internal method |
| Сила прокола пленки (50 µm) | 50.0 | N | Internal method |
| Сопротивление проколу пленки (50 µm) | 4.00 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 175 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 180 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 360 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 550 | % | ASTM D882 |
| Ударное падение Dart (50 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 460 | g | ASTM D1922 |
| TD : 50 µm, blown film | 290 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.0 µm, Blown Film) | 71 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 6.8 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：通用 输出：29 kg/h 模具直径：150 英寸 放大比：2.5 螺杆速度：74 rpm |
| Тип материала | Категория | Производитель |
|---|---|---|
| SABIC® LDPE 2022TN00 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| SABIC® LDPE 2201H3W | LDPE | Saudi Basic Industries Corporation (SABIC) |
| Purell PE 3220 D | LDPE | LyondellBasell Industries |
| TIPOLEN® FC 243-51 | LDPE | MOL Petrochemicals Co. Ltd. |
| CERTENE™ LDF-820A | LDPE | Muehlstein |
| Kazan LDPE 102-12K | LDPE | Kazanorgsintez Joint Stock Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved