Описание материалов:
MonoSol AF L337 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology.
MonoSol AF L337 is a highly plasticized grade of PVOH cold water-soluble packaging film with good film to film tack and is the film choice for stretch wrapping applications. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil).
MonoSol AF L337 is a highly plasticized grade of PVOH cold water-soluble packaging film with good film to film tack and is the film choice for stretch wrapping applications. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil).
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Содержание влаги (23 °C) 1 | 7.6 | wt% | |
| Растворимость 2 | |||
| Disintegration : 10°C, 50.0 µm | 24.0 | sec | |
| Disintegration : 24°C, 50.0 µm | 12.0 | sec | |
| Dissolution : 10°C, 50.0 µm | 83.0 | sec | |
| Dissolution : 24°C, 50.0 µm | 58.0 | sec |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Выход (50,0 мкм) | 16.1 | m²/kg | ASTM D4321 |
| Толщина пленки протестирована | 50 | µm | |
| Толщина пленки-рекомендовано/доступно | 20 µm to 60 µm | ||
| Сектантный модуль | ASTM D882, ISO 527-3 | ||
| 10%, MD : 50 µm | 49.6 | MPa | |
| 100%, MD : 50 µm | 17.2 | MPa | |
| 10%, TD : 50 µm | 43.4 | MPa | |
| 100%, TD : 50 µm | 8.96 | MPa | |
| Прочность на растяжение | |||
| MD : Break, 50 µm | 30.3 | MPa | ASTM D882 |
| TD : Break, 50 µm | 31.7 | MPa | ASTM D882 |
| MD : 50 µm | 30.3 | MPa | ISO 527-3 |
| TD : 50 µm | 31.7 | MPa | ISO 527-3 |
| Удлинение при растяжении | |||
| MD : Break, 50 µm | 230 | % | ASTM D882, ISO 527-3 |
| TD : Break, 5.0E-3 µm | 420 | % | ASTM D882 |
| TD : Break, 50 µm | 420 | % | ISO 527-3 |
| Elmendorf Tear Strength | |||
| MD : 50 µm | 1300 | g | ASTM D1922 |
| TD : 50 µm | 1500 | g | ASTM D1922 |
| MD : 50 µm | 0.13 | N | ISO 6383-2 |
| TD : 50 µm | 0.15 | N | ISO 6383-2 |
| Примечание | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Тип материала | Категория | Производитель |
|---|---|---|
| DENKA POVAL MP-10 | PVOH | Denka Company Limited |
| DENKA POVAL K-17C | PVOH | Denka Company Limited |
| Mowiol® 6-98 | PVOH | Kuraray Co., Ltd. |
| Kuraray Poval® PVA 105K | PVOH | Kuraray Co., Ltd. |
| Kuraray Poval® PVA 203 | PVOH | Kuraray Co., Ltd. |
| Selvol™ E 107 | PVOH | Sekisui Chemical Company, Ltd. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved