Описание материалов:
HMF-0856 is a certified prime grade Hexene copolymer MEDIUM MOLECULAR WEIGHT developed for production of thin gauged high stiffness paper-like Blown films. HMF-0856 features BROAD molecular weight distribution for improved processability at lower extruder pressure, excellent film drawdown, and good combination of high film stiffness with good film strength and improved barrier properties. HMF-0856 can be easily processed in HMW high stalk film equipment or in conventional film lines equipped with die gap = 0.75 to 1.25 = mm.. HMF-0856 applications include deli, meat & cheese wrap films, cereal box liners, notion and millinery bags, small shoppers, multi-wall and single liners, lamination films, coextrusion of films for stand-up-still pouches, and as substitute films for grease-proof waxed and acid free papers. Minimum recommended film gauge is 12 microns (0.5 mil), and processing temperature 195° to 205° C. HMF-0856 complies with FDR regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Сополимер
- Гексен-комномер
- Обрабатываемость, хорошая
- Широкое молекулярное распределение веса
- Хорошее Отшелушивание
- Соответствие пищевого контакта
- Средний Молекулярный вес
|
| Используется | - Пленка
- Ламинат
- Подкладка
- Сумка
- Пищевая упаковка
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Метод обработки | - Выдувная пленка
- Коэкструзионное формование
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.956 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 31 | µm | |
| Толщина пленки-рекомендовано/доступно | Minimum 12 µm (0.5 mil) | | |
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD
: 31 µm, blown film | 860 | MPa | ASTM D882 |
| 1% secant, TD
: 31 µm, blown film | 1040 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 31 µm, blown film | 24.0 | MPa | ASTM D882 |
| TD
: Yield, 31 µm, blown film | 14.0 | MPa | ASTM D882 |
| MD
: Broken, 31 µm, blown film | 52.0 | MPa | ASTM D882 |
| TD
: Broken, 31 µm, blown film | 19.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Broken, 31 µm, blown film | 570 | % | ASTM D882 |
| TD
: Broken, 31 µm, blown film | 490 | % | ASTM D882 |
| Ударное падение Dart 1(31 µm, blown film) | 75 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 31 µm, blown film | 15 | g | ASTM D1922 |
| TD
: 31 µm, blown film | 560 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура плавления | 130 | °C | ASTM D3417 |
| Дополнительная информация |
|---|
| Film Specimen: 1.25 mil (31 µm) film, melt temperature 410-440°F (210-225°C), blow-up-ratio 4.0:1, frost line height 8 x die ø. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 195 - 205 | °C | |