LUVOCOM® 50-0833

Категория	PC, Polycarbonate
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	9D7yVn_LUVOCOM-50-0833.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®50-0833 is a polycarbonate (PC) material, which contains glass and carbon fiber reinforced materials. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 50-0833 are:

Conductivity

Electrostatic protection

Good dimensional stability

Typical application areas include:

engineering/industrial accessories

business/office supplies

Sporting goods

medical/health care

Главная Информация
Наполнитель/армирование	Армированные материалы из стекла и углеродного волокна
Характеристики	Хорошая стабильность размеров Проводящий Защита от электростатического разряда
Используется	Шестерня Инженерные аксессуары Бизнес-оборудование Спортивные товары Медицинские принадлежности/принадлежности для ухода
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.33	g/cm³	ISO 1183
Формовочная усадка	0.20 - 0.50	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.20	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	9500	MPa	ISO 527-2
Tensile Stress (Break)	125	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.2	%	ISO 527-2
Флекторный модуль	8000	MPa	ISO 178
Флекторный стресс	185	MPa	ISO 178
Коэффициент трения
Dynamic	0.24
Static	0.22
Flexural Strain at Flexural Strength	3.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B
Викат Температура размягчения	160	°C	ISO 306/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+3	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки	120	°C
Время сушки	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	280 - 300	°C
Средняя температура	290 - 310	°C
Передняя температура	300 - 320	°C
Температура сопла	290 - 310	°C
Температура обработки (расплава)	295	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
PRL PC-FR-UV2	PC	Polymer Resources Ltd.
TRIREX® 3022L1(SB)	PC	Samyang Corporation
Iupilon® GSH2030SR 9920A	PC	Mitsubishi Engineering-Plastics Corp
Torayca® NX85T-10A	PC	Toray Resin Company
CALIBRE™ 2061-15	PC	Trinseo
LUVOCOM® 50/TF/15/NAT	PC	LEHVOSS Group

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

