Описание материалов:

LUVOCOM®1-8840 is a polyamide 66 (nylon 66) material, and the filler is glass fiber reinforced material. This product is available in Europe,.

LUVOCOM®The main features of 1-8840 are:

anti-warping

Good stiffness

Wear-resistant

heat stabilizer

Lubrication

Typical application areas include:

textile/fiber

engineering/industrial accessories

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал
Добавка	Ptfe лубрикант Стабилизатор тепла
Характеристики	Низкий коэффициент трения Низкий уровень защиты Жесткий, хороший Хорошая прочность Хорошая стойкость к истиранию Термическая стабильность Смазка
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.51	g/cm³	ISO 1183
Формовочная усадка	0.20 - 0.50	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 1.0	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	11000	MPa	ISO 527-2
Tensile Stress (Break)	157	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.5	%	ISO 527-2
Флекторный модуль	9000	MPa	ISO 178
Флекторный стресс	230	MPa	ISO 178
Коэффициент трения
Dynamic	0.20
Static	0.14
Flexural Strain at Flexural Strength	3.2	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	160	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	120	°C	UL 746B
Викат Температура размягчения	250	°C	ISO 306/A

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Время сушки
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.10	%
Задняя температура	290 - 310	°C
Средняя температура	290 - 310	°C
Передняя температура	290 - 310	°C
Температура сопла	280 - 300	°C
Температура обработки (расплава)	290	°C
Температура формы	90.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
DynaPath™ C2050CF	Nylon 66	Polymer Dynamix
RTP 200H TFE 15	Nylon 66	RTP Company
PRL NY66-IM1G13	Nylon 66	Polymer Resources Ltd.
UNITIKA Nylon 66 A175G15	Nylon 66	UNITIKA Plastics Division
DOMAMID® 66G30HUV	Nylon 66	DOMO Engineering Plastics SPA
TEKAMID™ TA631	Nylon 66	Mando Advanced Materials Co., Ltd.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

