Описание материалов:
Bayflex 906 is a fully compounded, water-blown, polyether-based polyurethane system consisting of two liquid components. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Bayflex 906 system was developed for use in a wide variety of applications requiring a microcellular core and a tough, abrasion-resistant outer surface. Examples of possible applications include appliance handles, office chair armrests, and dunnage strips. As with any product, use of the Bayflex 906 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Используется | |
| Формы | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shaw A, 12.7mm) | 66 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 12.7 mm) | 3.48 | MPa | ASTM D412 |
| Удлинение при растяжении (Break, 12.7 mm) | 150 | % | ASTM D412 |
| Tear Strength 1(12.7 mm) | 15.8 | kN/m | ASTM D624 |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта 2 | | | |
| Component a | Mixing ratio by weight: 73 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Specific Gravity @ 25°C: 1.21
Viscosity @25°C: 800 mPa
Flash Point, PMCC: 213°C
NCO: 22.6 to 23.1 wt%
Part B
Type: Polyol
Specific Gravity @ 25°C: 1.02
Viscosity @25°C: 1100 mPa-s
Flash Point, PMCC: 121°C
Water: 0.60 wt% max
Hydroxyl Number: 194: mg KOH/g
Material Temperatures: 25 to 40°CMold Temperature: 55 to 65°CDemold Time, 0.25 in thickness: 3.5 minLinear Shrinkage at 0.50 g/cm³: <0.5%Hand Mix Reactivity at 23°C
Cream Time: 50 sec
Tack-Free Time: 60 sec
Pull Time: 90 sec
Free-Rise Density: 11 to 16 lb/ft³ |
| Примечание |
|---|
| 1 . | C mould |
| 2 . | 98 Index |