LUVOCOM® 1850-7692/BK VP

Категория	PBT, Polybutylene Terephthalate
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	8U45LY_LUVOCOM18507692BKVP.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1850-7692/BK VP is a polybutene terephthalate (PBT) material containing glass beads. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 1850-7692/BK VP are: wear resistance.

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Микро стеклянная бусина
Характеристики	Низкий коэффициент трения Хорошая стойкость к истиранию
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование Камера
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.61	g/cm³	ISO 1183
Формовочная усадка	0.90 - 1.8	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	3000	MPa	ISO 527-2
Tensile Stress (Break)	33.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.8	%	ISO 527-2
Флекторный модуль	2400	MPa	ISO 178
Флекторный стресс	50.0	MPa	ISO 178
Flexural Strain at Flexural Strength	4.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	120	°C
Vacuum dryer, B	80	°C
Время сушки
Hot air dryer, A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Задняя температура	240 - 260	°C
Средняя температура	260 - 280	°C
Передняя температура	250 - 270	°C
Температура сопла	250 - 265	°C
Температура обработки (расплава)	250	°C
Температура формы	60 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
POLYshine PBT D204 GF30 FR	PBT	Polykemi AB
PTS PBT-1100	PBT	Polymer Technology and Services, LLC
RTP ESD A 1005 FR	PBT	RTP Company
TechnoDur PBT4 GF 20 Natural (9990)	PBT	TechnoCompound GmbH
POCAN® B 1700 000000	PBT	LANXESS GmbH
ESTOPLAST EP 1500WW06	PBT	Ester Industries Ltd.