LUVOCOM® 105-8990

Категория	TPE, Thermoplastic Elastomer
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	8AY7Cw_LUVOCOM-105-8990.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®105-8990 is a thermoplastic elastomer (TPE) material,. This product is available in Europe,.

LUVOCOM®The main features of 105-8990 are:

Conductivity

Electrostatic protection

Typical application areas include:

engineering/industrial accessories

House

Automotive Industry

Handle

Главная Информация
Характеристики	Проводящий Теплопроводность Защита от электростатического разряда
Используется	Ручка Инженерные аксессуары Ролик Применение в автомобильной области Чехол
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.32	g/cm³	ISO 1183
Массовый расход расплава (MFR) (250°C/10.0 kg)	3.0	g/10 min	ISO 1133
Формовочная усадка	0.60 - 1.2	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore D)	50		ISO 868

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	200	MPa	ISO 527-2
Tensile Stress (Break)	15.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	150	%	ISO 527-2

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1fU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	120	°C	UL 746B
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+13	ohms	IEC 60167

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Теплопроводность ¹	4.0	W/m/K

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+13	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки- Сушилка горячего воздуха, а	105	°C
Время сушки- Сушилка горячего воздуха, а	3.0 - 4.0	hr
Рекомендуемая максимальная влажность	0.010	%
Задняя температура	220 - 240	°C
Средняя температура	230 - 250	°C
Передняя температура	230 - 250	°C
Температура сопла	230 - 250	°C
Температура обработки (расплава)	240	°C
Температура формы	20.0 - 45.0	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Примечание
1 .	Hot-Disk, 60x60x3 mm

Тип материала	Категория	Производитель
Maxelast® P2630	TPE	Nantong Polymax Elastomer Technology, Co., Ltd
Monprene® IN-12985	TPE	Teknor Apex Company
Multi-Flex® TPE TES A5110 EU1	TPE	Multibase, A Dow Corning Company
Gallonprene® GP420-4001	TPE	Shenzhen Sungallon Rubber & Plastic Corporation Limited
Gallonprene® GP420-6003	TPE	Shenzhen Sungallon Rubber & Plastic Corporation Limited
StarFlex® 7045-1008	TPE	Star Thermoplastic Alloys & Rubbers, Inc.