Описание материалов:
.Pearlbond® 103 is a linear, polycaprolactone-based polyurethane, supplied in form of small white granules, which combines a very high crystallization rate with a very high thermoplasticity level. It is used for Hot Melt adhesives.
Pearlbond® 103 is mainly used for making heat-sealable fabrics (thermobonding), obtained by coating processes such as scattering or dot-coating (powder or paste). In all cases, the product is previously ground into powder, by cryogenic grinding. The particle size of the powder will depend on the application technique to be used.
Pearlbond® 103 is used for textile coating for making shoe-stiffeners (toe puffs & counters), by extrusion or sintering process.
| Главная Информация | |
|---|
| Характеристики | - Кристаллический
- Хорошая адгезия
- Термогерметичный
|
| Используется | - Клеи
- Нанесение покрытия
- Ткани
- Обувь
- Текстильные изделия
|
| Рейтинг агентства | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Покрытие
- Экструзия
- Покрытие разброса
- Спекание
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (20°C) | 1.19 | g/cm³ | ISO 2781 |
| Массовый расход расплава (MFR) (170°C/2.16 kg) | 60 to 100 | g/10 min | ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше (Shore D) | 51 | | ISO 868 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура плавления | 60.0 to 64.0 | °C | Internal Method |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Видимая вязкость 1(160°C) | 190 | Pa·s | ISO 1133 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость кристаллизации | Very High | | Internal Method |
| Softening Range | 55 to 60 | °C | Internal Method |
| Термопластичность | Very High | | Internal Method |