Trithene® TX 7003
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Petroquimica Triunfo |
| Торговая марка | Trithene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
7XGZgN_Trithene-TX-7003.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Trithene®TX 7003 is a low density polyethylene material,. This product is available in Latin America and is processed by film extrusion or blow molding.
Trithene®The main features of TX 7003 are:
Typical application areas include:
Trithene®The main features of TX 7003 are:
- high molecular weight
- Good processability
- accessible food
- Good dimensional stability
Typical application areas include:
- bag/lining
- Movie
- industrial applications
- bottle
- food contact applications
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.922 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение | ASTM D638 | ||
| Yield, molding | 11.0 | MPa | ASTM D638 |
| Fracture, molding | 17.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, Compression Molded) | 590 | % | ASTM D638 |
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | 0.45 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сектантный модуль | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 115 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 125 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 23.5 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 630 | % | ASTM D882 |
| Ударное падение Dart (50 µm, Blown Film) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 300 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 94.0 | °C | ASTM D1525 |
| Дополнительная информация |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 0.23 to 0.30 g/10 minDensity, ASTM D1505: 0.921 to 0.923 g/cm³ |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Зона цилиндра 1 темп. | 160 - 175 | °C | |
| Зона цилиндра 2 температура. | 170 - 185 | °C | |
| Зона цилиндра 3 темп. | 180 - 190 | °C | |
| Температура адаптера | 185 - 205 | °C |
| Инструкции по экструзии |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Тип материала | Категория | Производитель |
|---|---|---|
| TAISOX 6330F | LDPE | Formosa Plastics Corporation |
| 陶氏低密度聚乙烯 600C | LDPE | The Dow Chemical Company |
| KPOL-LDPE LD K-1.40/920 | LDPE | KPOL Chem Co. |
| Kazan LDPE 153 VSKM | LDPE | Kazanorgsintez Joint Stock Company |
| CERTENE™ LDF-0824B | LDPE | Muehlstein |
| Epolene® C-19 | LDPE | Westlake Chemical Corporation |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved