LUVOCOM® 50-8276

Категория	PC, Polycarbonate
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	7NUBXX_LUVOCOM-50-8276.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®50-8276 is a polycarbonate (PC) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 50-8276 are:

Good dimensional stability

Impact resistance

Lubrication

Typical application areas include:

engineering/industrial accessories

Electrical/electronic applications

Reflector

business/office supplies

Sporting goods

Главная Информация
Добавка	Ptfe лубрикант
Характеристики	Хорошая стабильность размеров Хорошая ударопрочность Смазка
Используется	Шестерня Зеркало Инженерные аксессуары Переключатель Бизнес-оборудование Спортивные товары Медицинские принадлежности/принадлежности для ухода
Внешний вид	Белый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.26	g/cm³	ISO 1183
Плавкий объем-расход (MVR) (300°C/1.2 kg)	15.0	cm³/10min	ISO 1133
Формовочная усадка	0.60 - 0.80	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.20	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	2200	MPa	ISO 527-2
Tensile Stress (Break)	50.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	5.0	%	ISO 527-2
Флекторный модуль	1800	MPa	ISO 178
Флекторный стресс	80.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	90	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	125	°C	ISO 75-2/A
Температура непрерывного использования	130	°C	UL 746B
Викат Температура размягчения	160	°C	ISO 306/A

Инъекция	Номинальное значение	Единица измерения
Температура сушки	120	°C
Время сушки	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	280 - 300	°C
Средняя температура	290 - 310	°C
Передняя температура	300 - 320	°C
Температура сопла	290 - 310	°C
Температура обработки (расплава)	295	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
RTP 305 EM	PC	RTP Company
TRIREX® Compound 3025AS	PC	Samyang Corporation
PC-COM™ PC415	PC	Polymer Compounders Limited
Makrolon® 2405 MAS048	PC	Covestro - Polycarbonates
XANTAR® 27 UR	PC	Mitsubishi Engineering-Plastics Corp
PermaStat® 307	PC	RTP Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

