Tenite™ Propionate 360A4861307 Clear, Trsp
Описание материалов:
Tenite™ Propionate 360A4861307 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulosic Acetate Propionate 360-7 has a plasticizer level of 7%.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Стерилизуемый e-луч
- Приемлемый пищевой контакт
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Хорошая прочность
- Высокая четкость
- Глянцевый
- Высокая твердость
- Пластифицированный
- Радиационный стерилизуемый
- Содержание возобновляемых ресурсов
- Мягкий
|
| Используется | - Медицинские/медицинские приложения
|
| Рейтинг агентства | - FDA пищевой контакт, неуказанный рейтинг
- ISO 10993
- USP класс VI
|
| Внешний вид | - Янтарь
- Черный
- Прозрачный/прозрачный
- Натуральный цвет
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.21 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 0.20 to 0.60 | % | ASTM D955 |
| Поглощение воды (23°C, 24 hr) | 1.7 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 95 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| Yield, 23°C | 41.4 | MPa | |
| Break, 23°C | 40.7 | MPa | |
| Удлинение при растяжении (Break, 23°C) | 50 | % | ASTM D638 |
| Флекторный модуль (23°C) | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 55.8 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C | 85 | J/m | |
| 23°C | 200 | J/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке 1 | | | ASTM D648 |
| 0.45 MPa, Annealed | 92.0 | °C | |
| 1.8 MPa, Annealed | 82.0 | °C | |
| Викат Температура размягчения 2 | 107 | °C | ASTM D1525 |
| CLTE-
Поток (23°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Удельный нагрев (23°C) | 1260 to 1670 | J/kg/°C | DSC |
| Теплопроводность 3(23°C) | 0.25 | W/m/K | ASTM C177 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Диэлектрическая прочность (23°C) | 12 to 19 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная (23°C, 1 MHz) | 3.30 to 3.80 | | ASTM D150 |
| Коэффициент рассеивания (23°C, 1 MHz) | 0.010 to 0.15 | | ASTM D150 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс преломления | 1.460 to 1.490 | | ASTM D542 |
| Коэффициент пропускания (1520 µm) | > 90.0 | % | ASTM D1003 |
| Haze (1520 µm) | < 8.5 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Потеря растворимого вещества (23°C) | 0.10 | % | ASTM D570 |
| Потеря веса при нагревании-
72 часа (80°C) | 0.30 | % | ASTM D1562 |
| Примечание |
|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| 2 . | Conditioned 4 hours at 70°C (158°F) |
| 3 . | Range: 0.17 to 0.33 |