Описание материалов:
Clearflex FF 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion.
Film manufactured with Clearflex FF 508 are characterised by excellent optical properties, if compared to the resin density, high rigidity and temperature resistance, optimum sealing properties.
Main Application
Due to its high optical, mechanical and sealing performances, Clearflex FF 508 is recommended for applications in which the high rigidity and the optimum gloss of this resin are a key factor (hygienic film, packaging for mineral water). The high Vicat softening point makes Clearflex FF 508 ideal for the production of film for food which is submitted to pasteurisation or sterilisation process.
| Главная Информация | |
|---|
| Добавка | - Антиоксидант
- Обработка помощи
|
| Характеристики | - Антиоксидант
- Сополимер
- Приемлемый пищевой контакт
- Хорошее тепловое уплотнение
- Высокая термостойкость
- Высокая жесткость
- Октеновый комномер
- Оптика
|
| Используется | |
| Рейтинг агентства | - ЕС пищевой контакт, неуказанный рейтинг
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.934 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | > 0.50 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Толщина пленки-рекомендовано/доступно | 10 to 50µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% Secant, MD
: 25 µm, Blown Film | 400 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 450 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 25 µm, Blown Film | 16.0 | MPa | |
| TD
: Yield, 25 µm, Blown Film | 18.0 | MPa | |
| MD
: Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD
: Break, 25 µm, Blown Film | 40.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 25 µm, Blown Film | 550 | % | |
| TD
: Break, 25 µm, Blown Film | 700 | % | |
| Ударное падение Dart 1(25 µm, Blown Film) | 90 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | | | ISO 6383-2 |
| MD
: 25.0 µm | 35.0 | kN/m | |
| TD
: 25.0 µm | 200.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 117 | °C | ISO 306/A |
| Температура плавления | 127 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 25.0 µm, Blown Film) | 60 | | ASTM D2457 |
| Haze (25.0 µm, Blown Film) | 12 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 190 to 230 | °C | |
| Примечание |
|---|
| 1 . | F50 |
| 2 . | Blown Film |