LUVOCOM® 1850-8023

Категория	PBT, Polybutylene Terephthalate
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	5nST7O_LUVOCOM-1850-8023.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1850-8023 is a polybutene terephthalate (PBT) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1850-8023 are:

Conductivity

Electrostatic protection

Good stiffness

Typical application areas include:

textile/fiber

engineering/industrial accessories

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Армированный материал из углеродного волокна
Характеристики	Проводящий Жесткий, хороший Защита от электростатического разряда Хорошая прочность
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.36	g/cm³	ISO 1183
Формовочная усадка	0.30 - 0.60	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	12000	MPa	ISO 527-2
Tensile Stress (Break)	105	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.3	%	ISO 527-2
Флекторный модуль	9500	MPa	ISO 178
Флекторный стресс	155	MPa	ISO 178
Flexural Strain at Flexural Strength	3.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	160	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 10	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	120	°C
Vacuum dryer, B	80.0	°C
Время сушки
A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	240 - 260	°C
Средняя температура	260 - 280	°C
Передняя температура	250 - 270	°C
Температура сопла	250 - 265	°C
Температура обработки (расплава)	250	°C
Температура формы	60.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
PTS PBT-15GF	PBT	Polymer Technology and Services, LLC
PTS PBT-15GFR-BK	PBT	Polymer Technology and Services, LLC
4DUR® 9K23100 HI	PBT	4Plas
LNP™ THERMOCOMP™ WF006 compound	PBT	SABIC Innovative Plastics
SPESIN® KP210	PBT	Kolon Plastics, Inc.
VALOX™ 4012G resin	PBT	SABIC Innovative Plastics Europe