Описание материалов:
Tritan™ EX401, specifically developed for the Infant Care market, is an amorphous copolyester with excellent appearance and clarity. Tritan™ EX401 contains a mold release derived from vegetable based sources. Its most outstanding features are clarity, excellent toughness, hydrolytic stability, and heat and chemical resistance. Tritan™ EX401 meets infant care sterilization requirements via boiling water or microwave steam sterilization. This new-generation copolyester can also be molded into various applications without incorporating high levels of residual stress. Combined with Tritan™ copolyester's outstanding chemical resistance and hydrolytic stability, these features give molded products enhanced durability in the dishwasher environment, which can expose products to high heat, humidity, and aggressive cleaning agents.
Tritan™ EX401 can be converted into parts using injection molding, injection stretch blow molding (ISBM), and extrusion blow molding techniques.
Tritan™ EX401 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Contact Eastman representative for details on global food contact regulatory clearances.
Eastman Tritan™ EX401 copolyester is included in Eastman Chemical Company's Customer Notification Procedure which details our policy for customer notification when significant changes are made in Tritan™ EX401 sold into the infant care market. This procedure provides the infant care industry an added layer of confidence in the consistent quality and performance of Tritan.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Сополимер
- Высокая ударопрочность
- Обрабатываемость, хорошая
- Хорошая химическая стойкость
- Теплостойкость, высокая
- Высокое разрешение
- Хорошая прочность
- Соответствие пищевого контакта
- Стабильность гидролиза
- Хорошая производительность при потере
- Хороший внешний вид
- Аморфный
- Паровая дезинфекция
|
| Используется | - Уход за младенцем
- Бутылка
- Резиновая соска
|
| Рейтинг агентства | - FDA пищевой контакт, не Номинальный
|
| Метод обработки | - Литье под давлением
- Экструзионное выдувное формование
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.17 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | | | |
| Blow Molded | 1.2 - 1.6 | % | Internal method |
| Injection Molding | 0.50 - 0.70 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 115 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 23°C | 1590 | MPa | ASTM D638 |
| 23°C | 1620 | MPa | ISO 527-2 |
| Прочность на растяжение | | | |
| Yield, 23°C | 44.0 | MPa | ASTM D638, Internal Methods |
| Yield, 23°C 1 | 45.0 | MPa | Internal Methods, ISO 527-2 |
| Fracture, 23°C | 53.0 | MPa | ASTM D638 |
| Fracture, 23°C | 49.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C 2 | 7.0 | % | Internal Methods, ASTM D638, ISO 527-2 |
| Yield, 23°C 3 | 6.5 | % | Internal method |
| Fracture, 23°C | 140 | % | ASTM D638 |
| Fracture, 23°C | 130 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 1590 | MPa | ASTM D790 |
| 23°C | 1530 | MPa | ISO 178 |
| Flexural Strength (Yield, 23°C) | 66.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 130 | J/m | ASTM D256 |
| 23°C | 650 | J/m | ASTM D256, Internal Methods |
| 23°C 4 | 640 | J/m | Internal method |
| -40°C | 14 | kJ/m² | ISO 180 |
| 23°C | 66 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4812 |
| -40°C | No Break | | ASTM D4812 |
| 23°C | No Break | | ASTM D4812 |
| Ударное устройство для дротиков | | | ASTM D3763 |
| -40°C, Energy at Max Load | 63.0 | J | ASTM D3763 |
| 23°C, Energy at Max Load | 59.0 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 109 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 92.0 | °C | ASTM D648 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания (Total) | 92.0 | % | ASTM D1003 |
| Haze | | | |
| -- 5 | < 1.0 | % | Internal method |
| -- | < 1.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сжатие объема заполнения 6 | | | Internal method |
| Boiling, 1 hr | | % | Internal method |
| Boiling, 2 hr | | % | Internal method |
| Dishwasher | | % | Internal method |
| Микроволновое кипячение-
Мощность печи 7 | | Watts | Internal method |
| Стерилизация микроволнового пара-
Общая энергия 8 | | W-min | Internal method |
| Тепловой шок-
Погружение в воду
(От 35 до 98 °C) 9 | No effect | | Internal method |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 88.0 | °C | |
| Время сушки | 4.0 - 6.0 | hr | |
| Температура обработки (расплава) | 260 - 282 | °C | |
| Температура формы | 38.0 - 66.0 | °C | |
| Инструкции по впрыску |
|---|
| Injection Stretch Blow Molding Parameters:Processing Melt Temperature: 270 to 285°CInjection Mold Temperature: 60 to 70°CPreform Temperature at Blow: 185 to 195°CPrimary Blow Pressure: 0.03 to 0.08 MPaBlow Mold Temperature: 80 to 90°CResidual stress under polarized light, Fringe Count, EMN: <=3 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 240 - 250 | °C | |
| Инструкции по экструзии |
|---|
| Extrusion Blow Molding Mold Temperature: 25 to 45°C |
| Примечание |
|---|
| 1 . | After re-equilibration |
| 2 . | After 8 hr boiling |
| 3 . | After re-equilibration |
| 4 . | After re-equilibration |
| 5 . | After 8 hr boiling |
| 6 . | ISBM Bottle |
| 7 . | ISBM Bottle |
| 8 . | ISBM Bottle |
| 9 . | ISBM Bottle |